Viscose acrylic fiber home textile fabric and preparation method thereof

A technology of acrylic fiber and viscose, which is applied in the field of its preparation, can solve the problems of wide fabric width, high actual cost, dyeing color, etc., and achieve the effect of small color difference between head and tail, uniform color, and short and dense fluff

Pending Publication Date: 2022-01-07
JIANGSU GOLDSUN TEXTILE SCI & TECH
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, acrylic blended fabrics are rarely used in the field of wide-width bedding and home textiles. Part of the reason is that the actual cost of acrylic blended fabrics is relatively high due to the high consumption of wide-width bedding fabrics. The fabric has internal indicators such as anti-pilling, dyeing, and strong damage that are not up to standard
[0003] Patent CN109208135 A "Weaving method of polyester and heating acrylic fiber interweaving home textile fabric", the invention interweaves cationic dyeable polyester yarn and heating acrylic fiber yarn, and makes full use of existing fibers to weave new fabrics through the improvement of process methods. The invention does not clearly provide the influence of the detailed technical parameters of spinning and dyeing and finishing on the performance of the fabric, and does not disclose the technical means of how to improve the anti-pilling performance of the fabric and what test method is used; in actual operation, the spinning of the fabric The yarn method, tightness, and yarn specifications also have a great influence on the pilling resistance of the finished fabric. When the fabric is woven according to the shape of the honeycomb structure described in the patent, it will be more likely to cause pilling and cause its performance to deteriorate ; Patent CN109235072A "cotton acrylic fiber parallel line wide-width sanding woven fabric and production method thereof", this invention discloses the jigger production technology of dyeing acrylic fiber with disperse cationic dyes and the cotton acrylic fiber parallel line wide width woven fabric sanding production technology, The width of the fabric is very wide, and the actual cost is relatively high, which is not conducive to wide application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Viscose acrylic fiber home textile fabric and preparation method thereof
  • Viscose acrylic fiber home textile fabric and preparation method thereof
  • Viscose acrylic fiber home textile fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] 106” / 40s×40s / 160×95, 4 / 1 satin, viscose: acrylic = 70:30, yarn twist 105 twists / 10cm.

[0029] 1. Pretreatment process

[0030] Singeing: one front and one reverse light singeing, the speed is 115m / min.

[0031] Desizing: Desizing with amylase, the dosage of α-amylase is 8g / L, the dosage of non-ionic penetrant is 1.5g / L, keep warm at 50-60℃ for 4-6h, and then wash with 5 grids of hot water at 70-80℃ , working solution pH5-6.

[0032] Bleaching: 100% hydrogen peroxide 1.5g / L, hydrogen peroxide stabilizer 1.5g / L, chelating dispersant 2.5g / L, heat preservation at 95-98°C for 60min, working solution pH 8-9.

[0033] Light sanding: The fabric is sanded in sequence, then ceramic sanded, and finally the cloth is produced. Among them, the cloth inlet tension is 9kg, the cloth outlet tension is 12kg, 2 rollers for sanding, 6 rollers for ceramics, the speed of sanding rollers is 1000r / min, the mesh number of sanding is 600 mesh, the speed of ceramic rollers is 1050r / min, and t...

Embodiment 2

[0042] 106” / 40s×40s / 160×95, 4 / 1 satin, viscose: acrylic = 60:40, yarn twist 110 twists / 10cm, siro compact spinning.

[0043] 1. Pretreatment process

[0044] Singeing: one front and one reverse light singeing, the speed is 120m / min.

[0045]Desizing: desizing with amylase, the dosage of α-amylase is 5g / L, the dosage of non-ionic penetrating agent is 1g / L, heat preservation and desizing at 50-60℃ for 4-6h, and then wash with 5 grids of hot water at 70-80℃, Working solution pH5-6.

[0046] Bleaching: 100% hydrogen peroxide 2g / L, hydrogen peroxide stabilizer 2g / L, chelating dispersant 3g / L, heat preservation at 95-98°C for 60min, working solution pH 8-9.

[0047] Light sanding: The fabric is sanded in sequence, then ceramic sanded, and finally the cloth is produced. Among them, the cloth inlet tension is 10kg, the cloth outlet tension is 13kg, 2 rollers for sanding, 6 rollers for ceramics, the speed of sanding rollers is 1000r / min, the mesh number of sanding is 500 mesh, the s...

Embodiment 3

[0056] 106” / 40s×40s / 160×95, 4 / 1 satin, viscose:acrylic=80:20, yarn twist 100 twist / 10cm, siro compact spinning.

[0057] 1. Pretreatment process

[0058] Singeing: one front and one reverse light singeing, the speed is 110m / min.

[0059] Desizing: Desizing with amylase, the dosage of α-amylase is 10g / L, the dosage of non-ionic penetrant is 2g / L, heat preservation and desizing at 50-60℃ for 4-6h, and then wash with 5 grids of hot water at 70-80℃, Working solution pH5-6.

[0060] Bleaching: 100% hydrogen peroxide 1g / L, hydrogen peroxide stabilizer 1g / L, chelating dispersant 2g / L, heat preservation at 95-98°C for 70min, working solution pH 8-9.

[0061] Light sanding: The fabric is sanded in sequence, then ceramic sanded, and finally the cloth is produced. Among them, the cloth inlet tension is 8kg, the cloth outlet tension is 11kg, 2 rollers for sanding, 6 rollers for ceramics, the speed of sanding rollers is 1000r / min, the mesh number of sanding is 600 mesh, the speed of cer...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention discloses a viscose acrylic fiber home textile fabric and a preparation method thereof. The fabric is prepared from viscose acrylic fiber blended yarn; and the viscose acrylic fiber blended yarn is composed of acrylic fibers and viscose fibers, wherein the ratio of the viscose fibers to the acrylic fibers is (80-60): (20-40). The preparation method of the viscose acrylic fiber home textile fabric comprises a spinning process, a weaving process and a dyeing and finishing process, wherein the dyeing and finishing process comprises pretreatment, dyeing and after-finishing; and a double-frequency-conversion flat cylinder dyeing machine is adopted as dyeing equipment. The viscose acrylic fiber home textile fabric is thick in hand feeling, short and dense in fluff, small in head and tail color difference and uniform in color; the dyeing and finishing processing method is relatively low in cost; and all inherent indexes of the fabric are qualified, and particularly the fabric is good in pilling resistance (circular track D method), shrinkage rate and linting rate.

Description

technical field [0001] The invention relates to a viscose acrylic fiber home textile fabric and a preparation method thereof. Background technique [0002] Acrylic fiber has always been known as artificial wool, and its soft and fluffy feel is used in clothing, carpets and other fields. Acrylic fiber can be blended with a variety of fibers, such as acrylic fiber can be blended with cotton fiber, modal, tencel, viscose, wool, polyester, nylon and other fibers with multi-component fibers to obtain different feel and style. Narrow-width knitted garment fabrics such as acrylic modal and acrylic viscose cotton are widely used in the market at present. However, acrylic blended fabrics are rarely used in the field of wide-width bedding and home textiles. Part of the reason is that the actual cost of acrylic blended fabrics is relatively high due to the high consumption of wide-width bedding fabrics. The fabric has internal indicators such as anti-pilling, dyeing, and strong damag...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06P1/41D06P1/653D06P1/673D06P3/85D06L1/14D06L4/13D06L4/12D03D15/225D03D15/283D03D15/47
CPCD06P1/41D06P1/6533D06P1/6735D06P3/8266D06L1/14D06L4/13D06L4/12D03D15/225D03D15/283D03D15/47D10B2201/24D10B2321/10
Inventor 胡青青陈红霞肖俐
Owner JIANGSU GOLDSUN TEXTILE SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products