Method of synthetizing lithium ion cell positive electrode material through solution burning

A technology for lithium-ion batteries and positive electrode materials, which is applied in the field of energy functional materials preparation, can solve the problems of uneven diffusion of transition metal ions in solid-phase reactions, energy-consuming and time-consuming synthesis of active materials, and high synthesis temperature, so as to reduce energy consumption and keep heat The effect of short time and fast self-burning speed

Inactive Publication Date: 2006-12-06
UNIV OF SCI & TECH BEIJING
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In these synthesis processes, there are problems such as high synthesis temperature, long holding time, as long as more than ten hours to several days, large energy consumption and uneven diffusion of transition metal ions in solid-state reaction, so the synthesis of active materials is energy-consuming and time-consuming.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method of synthetizing lithium ion cell positive electrode material through solution burning
  • Method of synthetizing lithium ion cell positive electrode material through solution burning
  • Method of synthetizing lithium ion cell positive electrode material through solution burning

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] 1. LiNO 3 (Analytical pure 99%) 2.537 grams, Co (NO 3 ) 2 ·6H 2 O (analytically pure 99%) 5.355 grams, Ni (NO 3 ) 2 ·6H 2 O (analytically pure 99%) 3.566 grams, citric acid (C 6 h 8 o 7 ·H 2 O) (analytical purity 99%) 5.724 g, made into 15 ml of aqueous solution, and electromagnetically stirred at 80° C. for 20 minutes.

[0018] 2. Move the solution from the evaporating dish into a muffle furnace that has been kept at 350°C. The solution absorbs heat and evaporates. After 5 minutes, it boils and burns, releasing yellow-brown gas, and the product is black and fluffy. Naturally cool down with the furnace, take out and lightly grind and granulate, then raise the temperature to 850°C at 100°C / hour and keep it for 6 hours to synthesize the sample LiCo 0.6 Ni 0.4 o 2 .

[0019] Synthetic sample LiCo 0.6 Ni 0.4 o 2 The XRD pattern such as figure 1 As shown, the diagram shows that the crystal form is complete, and its diffraction peak is sharp, indicating that ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

In the invention, nitrate is as oxidant; organic carboxylic acid is as fuel. Mixing water solution is prepared by according mol ratio lithium nitrate : nitrate M(NO3)2 : organic carboxylic acid = 1.0-1.2 : 1 : 0.5-2.5. Through burning reaction of solution, the following results are reached: each metallic ion is mixed evenly in atom level; active powder material of anode of lithium ion cell LiMO2(M=Co1-x, Nix, Co1-xMnx) in super fine granularity is obtained; holding temp and holding time can be reduced, and energy is saved.

Description

technical field [0001] The invention relates to a preparation method of energy functional materials, in particular to the preparation of positive electrode materials of lithium ion batteries. Background technique [0002] Among the commercialized lithium-ion battery cathode materials, LiCoO 2 The performance is the best, but due to the lack of cobalt resources and high price, and its actual use capacity is only half of the theoretical capacity, in order to improve performance and reduce costs, a lot of doping modification research has been carried out. The properties of Ni, Mn and Co are similar, the price is lower than Co, LiNiO 2 and LiMn 2 o 4 is following LiCoO 2 More compounds were studied later. However, the preparation of trigonal LiNiO 2 When it is easy to produce cubic LiNiO 2 , while making LiNiO 2 The practical application is very limited. LiMn 2 o 4 The main obstacle to the commercialization of electrode materials is their poor storage performance and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/04H01M4/48H01M4/58C01G1/02C01D15/02H01M4/50H01M4/52H01M10/36
CPCH01M4/525H01M4/505H01M10/0525Y02E60/122Y02E60/10
Inventor 王新东张立刘伯文李建玲王志高
Owner UNIV OF SCI & TECH BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com