Composite method of making honeycomb material by pipe

A technology of honeycomb materials and pipes, which is applied in the direction of cardboard articles, etc., can solve the problems of lack of versatility, inability to pull apart, product specification restrictions, etc., to ensure composite strength and overall quality, ensure uniform glue coating, and improve production efficiency Effect

Inactive Publication Date: 2007-08-01
张瑞国
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

No matter how high the degree of automation of the above process is, it still has a technical problem that is difficult to solve, that is, the product specifications produced are limited: (1) when the height (thickness) of the honeycomb paper core is above 100mm, there will be a pull Not open or unstable, the density is difficult to control
(2) When the paper weight of the paper core produced in general is above 80-180g / m2, it is difficult to stretch and shape the paper core when the height of the paper core is above 50mm
The production efficiency of this process is relatively high, and the plastic honeycomb honeycomb unit produced has good connection strength, but the specifications and materials of the honeycomb aperture and wall thickness are limited by equipment and molds, and are not universal, so a large investment in equipment and molds is required To produce products with corresponding specifications

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite method of making honeycomb material by pipe

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Embodiment 1: The making of paper honeycomb material.

[0018] As shown in Figure 1, the paper tubes 1 arranged in the same direction are bonded together by the adhesive 2 to form a honeycomb composite. The length of the paper tube can be relatively long, and the thickness of the honeycomb core can be obtained by longitudinally cutting the honeycomb composite Size, edge cut flush. Honeycomb materials of the same size can be spliced ​​to form a honeycomb body of a larger size.

[0019] According to the method of the present invention, the adhesive adopts the impregnated glue whose weight ratio of starch and water is 1:3-8. The drying and curing strength is 30-80°C, and natural sunlight can be used in summer.

Embodiment 2

[0020] Embodiment 2: The making of metal honeycomb material.

[0021] As shown in Figure 1, metal aluminum pipes 1 arranged in the same direction are bonded together by adhesive 2 to form a honeycomb composite. The thickness of the honeycomb material is obtained by cutting the honeycomb composite longitudinally to obtain the required size, and the edges are cut flush. When using metal aluminum tubes to make honeycomb materials, the surface of the aluminum tubes should be pretreated to remove dirt, grease and other anti-sticking substances. According to the method of the present invention, the adhesive adopts a single-component epoxy resin glue solution.

Embodiment 3

[0023] As shown in Figure 1, PVC pipes 1 arranged in the same direction are bonded together by adhesive 2 to form a honeycomb composite. The thickness of the honeycomb material is obtained by cutting the honeycomb composite longitudinally to obtain the required size, and the edges are cut flush. According to the method of the present invention, the adhesive used is composed of methyl ethyl ketone and PVC resin material, methyl ethyl ketone: PVC resin material=80:20 (weight ratio).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

This invention relates to a compound method to process beehive materials with tubes, which comprises the following steps: distributing the tubes to one direction into model box of frame or net shape; dipping the box with glue liquid; then taking out model box and dripping the over glue liquid; then pressing and drying the tubes with certain pressure; solidifying it into beehive parts and taking out beehive from the box.

Description

technical field [0001] The invention relates to a method for compounding honeycomb materials. Background technique [0002] The honeycomb structure is a masterpiece in the process of biological evolution in nature. It has the best material weight-to-space ratio, the best mechanical structure, specific strength, and specific stiffness. It has good sound insulation and heat insulation performance. It is widely used in aerospace, vehicles, and building materials. Partition walls, doors, furniture, packaging, etc. [0003] Representative honeycomb products are: [0004] Paper honeycomb is a core material made of paper materials, and then the required covering materials are compounded on both sides of the core material, such as color steel plate, gypsum board, plastic board, etc. The traditional paper honeycomb is to glue the paper longitudinally according to a certain pore size and compound it layer by layer, and then use a paper cutter to cut the honeycomb core strip of the r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B31D3/02
Inventor 许刚张景园刘昭清王子昌王云山刘富刚于源
Owner 张瑞国
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com