Composite insulating material

A technology of composite thermal insulation materials and raw materials, which is applied in thermal insulation, building components, etc., can solve the problems of insufficient adhesion of thermal insulation materials, insufficient thermal insulation effect, high thermal conductivity, etc., and achieve good sealing, thin material thickness, and high thermal conductivity. low effect

Inactive Publication Date: 2003-10-15
邱日平 +1
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] There are many insulation materials used for pipelines, equipment, and walls, but some still have high thermal conductivity, poor sealing, large leakage, etc., especially when used for some special-shaped equipment and pipelines. The adhesion of the material is not enough, it is easy to fall off, and the insulation effect is not good enough

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Take the raw materials according to the following weight ratio:

[0013] Aluminum silicate fiber 120kg Perlite 150kg Asbestos fiber 80kg Bentonite 150kg

[0014] Penetrant 10kg, appropriate amount of water

[0015] Production Method:

[0016] First dilute the penetrating agent with water according to the dosage of 5-7kg / m3, put the aluminum silicate fiber into it, soak for 10 hours, then stir it with other raw materials to form a thick fiber paste.

Embodiment 2

[0018] Take materials according to the following weight ratio:

[0019] Aluminum silicate fiber: 180kg Perlite: 130kg Asbestos fiber: 100kg Bentonite: 120kg

[0020] Penetrant 30kg Water appropriate amount.

Embodiment 3

[0022] Take materials according to the following weight ratio:

[0023] Aluminum silicate fiber: 140kg Perlite: 140kg Asbestos fiber: 95kg Bentonite: 130kg

[0024] 20kg of penetrating agent and appropriate amount of water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
shrinkageaaaaaaaaaa
Login to view more

Abstract

The composite heat insulating material is fibrous thick paste produced with aluminum silicate fiber 10-18 weight portions, pearlite 12-16 weight portions, asbestos fiber 8-12 weight portions, bentonite 10-15 weight portions, permeating agent 1-3 weight portions and proper amount of clear water. The present invention has the advantages of low heat conducting coefficient, high heat insulating performance, no crack, high sealing performance and less falling, and is especially suitable for use in pipeline, apparatus, furnace and kiln in complicated shape.

Description

technical field [0001] The invention belongs to a composite thermal insulation material. Background technique [0002] There are many insulation materials used for pipelines, equipment, and walls, but some still have high thermal conductivity, poor sealing, large leakage, etc., especially when used for some special-shaped equipment and pipelines. The adhesion of the material is not enough, it is easy to fall off, and the insulation effect is not good enough. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a composite thermal insulation material with low thermal conductivity, not easy to crack, good sealing performance and not easy to fall off. [0004] The technical solution for solving the above problems is: the present invention is a fiber-thick paste made of the following weight ratio raw materials: [0005] Aluminum silicate fiber: 10-18 parts Perlite: 12-16 parts Asbestos fiber: 8-12 parts [0006] Benton...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B30/02E04B1/76
CPCC04B30/02
Inventor 邱日平赖永斌
Owner 邱日平
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap