Silicon-barium-strontium-calcium-magnesium-iron alloy as deoxidant in steelmaking
A technology of ferroalloy and deoxidizer, which is applied in the field of ferroalloy, silicon barium strontium calcium magnesium iron alloy, can solve the problems of affecting steel quality, insufficient desulfurization ability of silicon barium alloy, high price, etc., and achieve the effect of preventing splashing and hurting people
Inactive Publication Date: 2003-11-19
本溪冶炼厂
View PDF1 Cites 7 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
It has gradually developed from single deoxidation with aluminum to binary, ternary and multi-component composite deoxidized alloys, but these products can only play a role in deoxidation, and the price is relatively high. Phosphorus, which affects the quality of steel
[0003] Silicon-barium alloy is well known as a deoxidizer, although it has a fairly good deoxidation ability, it still cannot meet the further requirements for the oxygen content of molten steel
In addition, the desulfurization ability of existing silicon-barium alloys is obviously insufficient
At present, the published Chinese invention patent application No. 99109706.8 provides that the silicon-barium-magnesium-iron alloy used as a deoxidizer for steelmaking contains 2 to 8% aluminum, which requires aluminum-free steel types and acid-melted aluminum in steel for smelting. It is unfavorable for steel grades with very low content and strict
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0018] Adopt the preparation method that the present invention provides, the chemical composition (weight %) of the silicon barium strontium calcium magnesium iron alloy of smelting output is: Si 45.6%, Ba 25.3%, Sr 5.6%, Ca 6.1%, Mg 6.8%, balance For Fe.
Embodiment 2
[0020] Adopt the preparation method that the present invention provides, the chemical composition (weight %) of the silicon barium strontium calcium magnesium iron alloy of smelting output is: Si 47.2%, Ba 22.6%, Sr 6.1%, Ca 8.3%, Mg 10.5%, balance For Fe.
[0021] Above embodiment all obtains better technical and economic effect through a certain steel mill trial.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
Description
technical field [0001] The invention relates to a ferroalloy used as a steelmaking deoxidizer, in particular to a silicon-barium-strontium-calcium-magnesium-iron alloy used as a steelmaking deoxidizer, which is a supplement to existing ferroalloy varieties and belongs to the technical field of steelmaking. Background technique [0002] In recent years, the deoxidizers used for making killed steel have developed rapidly and have good effects. It has gradually developed from single deoxidation with aluminum to binary, ternary and multi-component composite deoxidized alloys, but these products can only play a role in deoxidation, and the price is high. In addition, although the molten steel for steelmaking still has a certain amount of sulfur, Phosphorus, thus affecting the quality of steel. [0003] Silicon-barium alloy is known as a deoxidizer, although it has a fairly good deoxidation ability, it still cannot meet the further requirements for the oxygen content of molten st...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More IPC IPC(8): C21C7/06
Inventor 姜殿波
Owner 本溪冶炼厂