Glaze material for color permeated polishing tile and application method thereof
A technology for polishing tiles and glazes, which is applied in the crafts and decorative arts for producing decorative surface effects, can solve the problems of lack of expressiveness, dull texture, monotonous color of seepage polished tiles, etc., and achieves good apparent quality. , fine texture, rich color effect
Inactive Publication Date: 2005-01-19
毛海燕
View PDF1 Cites 4 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0002] The color of the bleed polished tile produced by the glaze of the prior art is relatively monotonous, the texture is flat, and the expressive force is not rich; such as the application number is 99113799, the application date is June 21, 1999, and the invention name is full vitrified bleed A patent application for porcelain polished tiles, which consists of the following formula (percentage by weight): clay 30% to 35%, feldspar 45% to 50%, pyrophyllite 10% to 15%, magnesia mud 3% to 5%, kaolin 5%~10%, color stabilizer 0.2%~1%, color developing agent 0.5%~5%
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0015] The glaze used for the oozing polished tile of the present invention adopts copper salt and nickel salt as the base material, adds sodium citrate or ammonium citrate, and adopts A and B glazes to react, wherein A glaze: nickel acetate 30 grams of citric acid 45 grams of sodium, 100 grams of water, 100 grams of methyl, 2.5 grams of ethylene glycol, 15 grams of ethylene glycol, nickel acetate and sodium citrate are dissolved in water, methyl is dissolved in ethylene glycol and the two solutions are mixed and stirred; Print on the brick body; take B glaze: nickel acetate 20g sodium citrate 20g water 100g methyl 2.5g ethylene glycol 15g, mix B glaze in the same way as A glaze, take the above mixed B glaze for use Large-area nets are printed on the brick body; spray 100 grams of water (relative to a brick with a size of 600mm×600mm).
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention discloses a glaze material for color permeated polishing tile and application method thereof, wherein the glaze is made from glaze A and B through reaction, wherein glaze A comprises (by weight percentage) nickel acetate 20-50g, sodium citrate 30-60g, water 80-120g, methyl 1.5-3.5g, ethylene glycol 6-15g, while glaze B comprises (by weight percentage) nickel acetate 10-30g, sodium citrate 10-30g, water 80-120g, methyl 1.5-3.5g, ethylene glycol 6-15g.
Description
technical field [0001] The invention relates to a glaze used for bleed polished tiles and a using method. Background technique [0002] The color of the bleed polished tile produced by the glaze of the prior art is relatively monotonous, the texture is flat, and the expressive force is not rich; such as the application number is 99113799, the application date is June 21, 1999, and the invention name is full vitrified bleed A patent application for porcelain polished tiles, which consists of the following formula (percentage by weight): clay 30% to 35%, feldspar 45% to 50%, pyrophyllite 10% to 15%, magnesia mud 3% to 5%, kaolin 5% to 10%, color stabilizer 0.2% to 1%, color developing agent 0.5% to 5%. Above-mentioned patent has the above-mentioned defect equally. Contents of the invention [0003] The object of the present invention is to provide a glaze for the bleed polished tiles, which can make the texture of the bleed polished tiles more delicate, richer in color and...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): B44C1/24C03C8/00
Inventor 毛海燕
Owner 毛海燕