Artificial stone panel and manufacturing method thereof

A technology of artificial stone and panels, which is applied in imitation stone door panels, window frames, floors or handicrafts and their manufacture, door frames, and desktops. It can solve the problems of difficult transportation and installation, insufficient lightness of the product, and excessive stone powder, etc., and achieve low cost. , excellent wear resistance, good gloss effect

Inactive Publication Date: 2008-12-24
覃庆峰
View PDF6 Cites 28 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These imitation jade decorative materials can replace part of wood and steel, and have achieved success in utilizing resource-rich inorganic materials, but the shortcomin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Artificial stone panel and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0046] Example 1-1

[0047] First modify the aluminum hydroxide and calcium carbonate, and use dynamic (fluidized bed) heating method to increase the temperature of aluminum hydroxide and calcium carbonate to 80℃-130℃. 20 parts by weight of aluminum hydroxide over 200 mesh and 50 parts by weight of calcium carbonate over 500 mesh. 30 (weight) parts of polysiloxane modifier vinyl trichlorosilane are atomized into aluminum hydroxide and calcium carbonate to maintain Between 80-130°C, continue to boil in a fluidized bed for 2-6 minutes to obtain surface-modified aluminum hydroxide powder and calcium carbonate powder.

Example Embodiment

[0048] Example 1-2

[0049] In the dynamic (fluidized bed) heating method, when the temperature of aluminum hydroxide is 80℃-130℃, under its high-speed dynamic condition, according to 70 parts (weight) of aluminum hydroxide, 30 (weight) A part of polysiloxane modifier 3-(methacryloxy)propyltrimethoxysilane was added to 200 mesh aluminum hydroxide by atomization method, kept at 80-130℃, and continued to fluidize The bed is boiling, and the holding time is 2-6 minutes to obtain surface-modified aluminum hydroxide powder.

Example Embodiment

[0050] Example 1-3

[0051] In the dynamic (fluidized bed) heating method, when the temperature of calcium carbonate is 80℃-130℃, under its high-speed dynamic condition, according to 70 parts (weight) calcium carbonate, 30 (weight) parts are polymerized The siloxane modifier 3-aminopropyltrimethoxysilane was added to 200 mesh aluminum hydroxide by atomization method, kept at 80-130℃, and continued to boil in the fluidized bed for 2-6 minutes , To obtain surface modified calcium carbonate powder.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a artificial stone plate prepared by adding cobalt naphthenate accelerator, methylethylketone, light stabilizer, paint and antioxidant into unsaturated polyester resin. The preparation method includes the following steps: firstly modifying the aluminium hydroxide and/or calcium carbonate to get surface modified aluminium hydroxide and/or calcium carbonate or pure aluminium hydroxide powder, then adding cobalt naphthenate accelerator, methylethylketone, light stabilizer, paint and antioxidant into unsaturated polyester resin, uniformly mixing and stirring the mixture in a high speed stirring reactor, adding surface modified aluminium hydroxide and/or calcium carbonate powder or pure aluminium hydroxide powder, stirring and casting the mixture into a mould after vacuum defoamtion, heating up to 60-80 DEG C and curing to get the artificial stone and marble panel.

Description

technical field [0001] The invention relates to an artificial material, in particular to imitation stone door panels, desktops, door frames, window frames, floors or handicrafts made of non-metallic minerals and organic materials and a manufacturing method thereof. Background technique [0002] For a long time, the hotels, residences, offices and entertainment places built by people need to use a lot of wood. In addition to cement or stone for walls and roofs, columns or floors, a large number of building materials use wood and metal materials, especially door panels. , desktops, door and window frames, etc., so the demand for wood in our country is increasing year by year. According to statistics, in recent years, my country's annual wood consumption has exceeded 300 million cubic meters. The cutting limit is only 1.4 cubic meters; and aluminum alloy and steel are becoming more and more expensive with the gradual reduction of mineral resources. Therefore, in recent years, the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B26/10C04B14/36C04B14/28
CPCC04B26/18C04B2111/54
Inventor 覃庆峰
Owner 覃庆峰
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap