No-curing high-performance ceramic water-based paint and preparation method thereof

A high-performance, ceramic technology, applied in anti-corrosion coatings, fire-retardant coatings, coatings, etc., can solve the fundamental problems of nano-ceramic coatings that have not been well solved, and achieve reliable protective performance and decorative performance, high application value. , various effects

Inactive Publication Date: 2019-06-11
常州穗时新材料有限公司 +1
View PDF3 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although similar papers and patents are often reported, the fundamental problems of nano-ceramic coatings have not been well resolved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • No-curing high-performance ceramic water-based paint and preparation method thereof
  • No-curing high-performance ceramic water-based paint and preparation method thereof
  • No-curing high-performance ceramic water-based paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-2

[0033] Preparation of component A: according to the formula shown in Table 1, mix and stir each component evenly, and then filter;

[0034] Component B is made from commercially available raw materials, mixed and stirred uniformly;

[0035] Preparation of component C: According to the formula in Table 1, add all the raw materials except the toughened emulsion into the ladle, stir evenly, grind the color paste to a fineness below 20 μm in the high-speed dispersing equipment, discharge, and measure After the toughened acrylic emulsion is mixed and stirred evenly, it is the C component;

[0036] Mix components A and B at a ratio of 1:1, stir and react at a speed of 1200r / min for 5 minutes, add to component C and stir evenly, filter with a 100-mesh filter, and use it for spraying. In terms of mass ratio, A Component: B component: C component = 1:1:2;

[0037] The base material is (1) 2mm thick aluminum plate, polished with 300 mesh sandpaper after degreasing and degreasing; (2) ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to no-curing high-performance ceramic water-based paint and a preparation method thereof. The coating has is composed of an A component, a B component and a C component; the A component is prepared by mixing the following raw materials, in parts by weight: an acidic silica sol, an acidic aluminum sol, an acidic zirconium sol or a mixture of the acidic silica sol, the acidic aluminum sol and the acidic zirconium sol in any ratio, deionized water and an alcohol solvent, and performing dispersion; the B component is composed of the following materials: methyltrialkoxysilane,phenyltrialkoxysilane, tetraalkoxysilane, dimethyldialkoxysilane, diphenyldialkoxysilane, a silane coupling agent, an non-sticking auxiliary agent and a catalyst; and the C component is prepared by mixing the following raw materials: deionized water, isopropanol or ethanol, an acidic silica sol, a neutral silica sol or a mixture of the acidic silica sol and the neutral silica sol in any ratio, aninorganic filler, a coloring pigment, a toughening emulsion, a dispersant and other auxiliary agents, and performing dispersion. The paint provided by the invention does not need curing, has simple and convenient construction, excellent performance and good environmentally-friendly performance, and is easy to produce in a large scale, thereby being a novel high-performance water-based coating.

Description

technical field [0001] The invention relates to the field of new fluorosilicon materials, in particular to a curing-free high-performance ceramic water paint and a preparation method thereof. Background technique [0002] Under the background of my country's unprecedentedly strict environmental protection policies and people's increasing awareness of safety and health, high-performance water-based paints that use water as a dispersion medium and water-soluble / water-dispersible resins as film-formers have ushered in unprecedented opportunities for development. Nano-ceramic coatings are made of siloxane monomers or oligomers, supplemented with inorganic nanoparticles and high-temperature-resistant pigments and fillers, prepared by the sol-gel method, showing many common water-based coatings and even solvent-based coatings. Advantages, such as high temperature resistance, flame retardant and smokeless, high hardness, friction resistance, excellent weather resistance and gloss a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D183/04C09D5/08C09D5/18
Inventor 陈子辉李林芳缪国元薛亚波
Owner 常州穗时新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com