Electrolyte for rechargeable lithium battery and rechargeable lithium battery comprising same
An electrolyte and lithium battery technology, applied in secondary batteries, battery pack components, circuits, etc., can solve problems such as lack of ionic conductivity
Inactive Publication Date: 2005-01-19
SAMSUNG SDI CO LTD
View PDF3 Cites 4 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
However, this silicone oil does not have sufficient ionic conductivity for use in electrolytes for rechargeable lithium batteries
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0156] 10% by volume of oil 1 shown in Formula 7 was added to the non-aqueous electrolyte of Comparative Example 1 to prepare a non-aqueous electrolyte.
Embodiment 2
[0158] 10% by volume of the oil 2 represented by Formula 8 was added to the non-aqueous electrolyte of Comparative Example 1 to prepare a non-aqueous electrolyte.
Embodiment 3
[0160] 0.2 wt% of PAA and 1 wt% of TAZO were added to the non-aqueous electrolyte of Example 1 to prepare a non-aqueous electrolyte.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| flash point | aaaaa | aaaaa |
| flash point | aaaaa | aaaaa |
Login to View More
Abstract
Disclosed is a non-aqueous electrolyte for a rechargeable lithium battery including a polyether-modified silicon oil in which a polyether chain is bonded to a terminal end of a linear polysiloxane, a cyclic carbonate, and a lithium salt.
Description
[0001] Cross References to Related Applications [0002] This application claims Japanese Application Nos. 2003-003047 and 2003-363591 filed with the Japan Patent Office on Jan. 9, 2003 and Oct. 23, 2003 and Korean Application No. 2003 filed with the Korean Intellectual Property Office on Dec. 23, 2003 Priority of -97895, the entire disclosure of which is hereby incorporated by reference. field of invention [0003] The present invention relates to an electrolyte for a rechargeable lithium battery and a rechargeable lithium battery containing the electrolyte, and more particularly, to an electrolyte for a rechargeable lithium battery having good thermal safety and ionic conductivity and rechargeable lithium batteries containing this electrolyte. Background of the invention [0004] Usually, the organic solvent in the electrolyte uses one selected from cyclic esters such as ethylene carbonate or propylene carbonate, linear esters such as dimethyl carbonate or propionate, or ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): H01M2/16H01M10/0525H01M10/0567H01M10/0569H01M10/36
CPCH01M10/0567H01M10/0525H01M10/0569Y02E60/10
Inventor 郑喆洙山口滝太郎清水竜一
Owner SAMSUNG SDI CO LTD
Features
- Generate Ideas
- Intellectual Property
- Life Sciences
- Materials
- Tech Scout
Why Patsnap Eureka
- Unparalleled Data Quality
- Higher Quality Content
- 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com