Portland cement of industrial tailing
A technology of Portland cement and industrial tailings, applied in the field of cement, can solve the problems of polluting the environment and occupying cultivated land, achieve the effects of reducing production costs, reducing cultivated land occupation and environmental pollution, and improving the stability of cement
Inactive Publication Date: 2005-05-18
夏根华
View PDF0 Cites 18 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
The accumulation and discharge of huge tailings not only occupy arable land and pollute the environment, but also impose a huge burden on the country and enterprises
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0024] Ordinary Portland cement is made by mixing cement clinker, gypsum and treated tailings containing silica, calcium oxide and magnesium oxide according to the following weight ratio, and grinding to 80μm sieve ≤ 3%:
[0025] Cement clinker 81%, gypsum 4%, copper iron ore tailings 15%. Among them, copper iron ore tailings can be dried.
Embodiment 2
[0027] Composite Portland cement: 66% of cement clinker, 4% of gypsum, 10% of fly ash or slag, 20% of lead-zinc ore tailings; the rest are the same as in Example 1.
Embodiment 3
[0029] Pozzolanic Portland cement: 66% cement clinker, 4% gypsum, 30% copper iron ore tailings. All the other are with embodiment 1.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The industrial tailing cement is prepared with cement clinker, gypsum and treated Ca-Mg tailing in certain proportion, and through mixing, and grinding to 80 micron size. The tailing content is 6-15 wt% in portland cement, 15-50 wt% in composite portland cement, 20-50 wt% in gaize cement, 20-50 wt% in portland blast furnace slag cement, and 20-50 wt% in type-II portland cement. The cement with industrial tailing is easy to produce hydrated silicate, has high technological indexes, especially cement stability.
Description
Technical field [0001] The invention relates to cement, especially cement made from industrial tailings. Background technique [0002] The known Portland cement is made by mixing Portland cement clinker, gypsum and fly ash or slag according to a certain ratio, and grinding them. A certain proportion of fly ash or slag is used as a mixed material in cement, mainly to use its hydration activity to generate hydrated silicate, and to produce different standard cements that meet national regulations. In fact, there is another kind of material that can be used as a good cement mixture material, that is, the tailings of metal mines. Generally speaking, more than 80% of the tailings produced by ore mining after beneficiation are discharged and piled up as industrial waste residues. In my country, the annual discharge of the above-mentioned tailings is difficult to calculate, and the current accumulation volume has reached several billion tons. The accumulation and discharge of hu...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): C04B7/04C04B7/12C04B7/14C04B7/24
CPCY02P40/10
Inventor 王学武夏根华
Owner 夏根华