Energy-saving cement clinker quick sintering intensifier

A technology of cement clinker and reinforcing agent, which is applied in the field of cement clinker reinforcing agent to achieve the effect of accelerating formation, increasing output, and increasing early and late strength

Inactive Publication Date: 2010-06-09
XIAN DELAIKE CONCRETE ADDITIVE
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there is no catalytic material that can be used in the dry rotary kiln cement clinker production process, which can not only increase production but also save energy and enhance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Prepare 1000 kg of the product of the present invention: take by weighing 50 kg of rare earth ore, 250 kg of fluorite ore, 200 kg of barium slag, 200 kg of copper slag, 200 kg of lead-zinc slag, and 100 kg of steel slag. The above-mentioned raw materials are crushed to 3-5mm, then sieved, measured, mixed evenly, measured, packaged and formulated into an energy-saving cement clinker fast-burning enhancer.

Embodiment 2

[0018] Prepare 1000 kg of the product of the present invention: take by weighing 150 kg of rare earth ore, 100 kg of fluorite ore, 300 kg of barium slag, 250 kg of copper slag, 150 kg of lead-zinc slag, and 50 kg of steel slag. The above-mentioned raw materials are crushed to 3-5mm, then sieved, measured, mixed evenly, measured, packaged and formulated into an energy-saving cement clinker fast-burning enhancer.

Embodiment 3

[0020] Prepare 1000 kg of the product of the present invention: take by weighing 100 kg of rare earth ore, 130 kg of fluorite ore, 300 kg of barium slag, 200 kg of copper slag, 200 kg of lead-zinc slag, and 70 kg of steel slag. The above-mentioned raw materials are crushed to 3-5mm, then sieved, measured, mixed evenly, measured, packaged and formulated into an energy-saving cement clinker fast-burning enhancer.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an energy-saving cement clinker quick sintering intensifier, which is prepared into a finished product through the steps of crushing, screening, metering, uniformly mixing, metering and packing rear earth ores, fluorite mines, barium slag, copper slag, lead-zinc slag and steel slag which are in certain weight percentages. The energy-saving cement clinker quick sintering intensifier is a granular and powdery, nontoxic, harmless and radiation-free inorganic nonmetallic material which consists of a plurality of catalytic components and trace elements. When the product is used for a dry-process rotary kiln, the product can greatly improve the rate of dissolution of calcium carbonate, reduce the content of f-CaO, improve the yield per hour of the kiln by 10 to 30 percent, improve the early strength of clinkers by 3 to 7 MPa, keep the later strength of the clinkers about 60 MPa, reduce the sintering temperature of the clinkers by 50 to 100 DEG C, reduce coal consumption by 5 to 15 percent and reduce power consumption by 10 to 20 percent.

Description

technical field [0001] The invention relates to a cement clinker reinforcing agent, in particular to an energy-saving cement clinker quick-burning reinforcing agent used in the cement clinker firing process of a dry method rotary kiln. Background technique [0002] With the increase of national basic investment, the cement industry presents a situation of both production and sales. How to increase the output per kiln hour, reduce the energy consumption of cement production, and improve the quality of cement clinker has always been the goal pursued by researchers. At present, there is no catalytic material that can be used in the dry rotary kiln cement clinker production process, which can not only increase production but also save energy and strengthen. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide an energy-saving system that can increase the output of cement clinker, increase the strength of cement clinker, a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B7/42
Inventor 黄春江闵宝琦尚红彦
Owner XIAN DELAIKE CONCRETE ADDITIVE
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com