Method for manufacturing soft magnet silicon-aluminium magnetic powder core

A manufacturing method and magnetic powder core technology, which is applied in the direction of inductance/transformer/magnet manufacturing, inorganic material magnetism, electrical components, etc., can solve the problems of low toughness, iron core cracking, breaking, and large iron core loss, and achieve solidification Less stress, less mold release force, and increased cost

Inactive Publication Date: 2005-06-01
王锋 +1
View PDF0 Cites 39 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, with the rapid development of switching power supplies and UPS, it requires magnetic components with high magnetic permeability, high saturation magnetic flux density, low loss when operating at high frequency, and a small decrease in magnetic permeability after adding a DC bias magnetic field. A large number of iron powders are used. The core generally has low magnetic permeability (for μe=75), and the core loss is relatively large
The magnetic permeability of the sendust magnetic powder core can reach μe=125, the saturation magnetic flux density is about 1.5T (Tesla), and the magnetostriction coefficient is close to zero. Now, in order to obtain a good soft magnetic silicon-aluminum magnetic powder core, use There are many methods with complex processes, but the disadvantages of sendust are high brittleness, low toughness, narrow composition range, high sensitivity to heat treatment temperature, easy peeling off of molded molding, and it is in a loose state. If it is directly wound on the iron core, then The iron core will be cracked and broken, resulting in magnetic deterioration

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The manufacturing method of the soft magnet silicon-aluminum magnetic powder core of the present invention comprises:

[0029] 1. Magnetic particle size distribution:

[0030] -100 mesh to +150 mesh 15kg, -150 mesh to +250 mesh 60kg, -250 to +320 mesh 20kg, -320 5kg and mix well.

[0031] 2. Magnetic powder surface treatment:

[0032] Soak 100kg of uniformly mixed magnetic powder with 0.1-0.2% chromic anhydride aqueous solution for 10 minutes, bake in an oven at 100°C for 1.5 hours to dry.

[0033] 3. Magnetic powder, insulating agent, adhesive, release agent, mix well.

[0034] Add 1.5kg of -300 mesh mica powder to 100kg of magnetic powder, and then add 1kg of binder. Release agent 0.8kg, placed in the built-in mixer and stirred evenly.

[0035] 4. Compression molding:

[0036] Put the magnetic powder material containing insulating agent, adhesive and release agent that has been stirred and mixed evenly into the mold, and use 25t / cm 2 pressure molding.

[0037] ...

Embodiment 2

[0052] The manufacturing method of the soft magnet silicon-aluminum magnetic powder core of the present invention comprises:

[0053] 1. Magnetic particle size distribution:

[0054] -100 mesh to +150 mesh 10kg, -150 mesh to +250 mesh 40kg, -250 to +320 mesh 25kg, -320 25kg and mix evenly.

[0055] 2. Magnetic powder surface treatment:

[0056] Soak 100kg of magnetic powder mixed evenly with 0.5% chromic anhydride aqueous solution for 6 minutes, and bake in an oven at 120°C for 1 to 3 hours to dry.

[0057] 3. Magnetic powder, insulating agent, adhesive, release agent, mix well.

[0058] Add 1 kg of -300 mesh mica powder to 100 kg of magnetic powder. Then add 1 kg of binder. Release agent 1.2kg, placed in the built-in mixer and stirred evenly.

[0059] 4. Compression molding:

[0060] Put the magnetic powder material containing insulating agent, adhesive and release agent that has been stirred and mixed evenly into the mold, and use 22t / cm 2 pressure molding.

[0061] ...

Embodiment 3

[0075] The manufacturing method of the soft magnet silicon-aluminum magnetic powder core of the present invention comprises:

[0076] 1. Magnetic particle size distribution:

[0077] -100 mesh to +150 mesh 12kg, -150 mesh to +250 mesh 50kg, -250 to +320 mesh 23kg, -320 15kg and mix well.

[0078] 2. Magnetic powder surface treatment:

[0079] Soak 100kg of magnetic powder mixed uniformly with 0.9% chromic anhydride aqueous solution for 3 minutes, and bake in an oven at 150°C for 1 hour to dry.

[0080] 3. Magnetic powder, insulating agent, adhesive, release agent, mixed evenly:

[0081] Add 1.2kg of -300 mesh mica powder to 100kg of magnetic powder material, then add 1kg of binder and 0.8kg of release agent, and put it in a built-in mixer to stir and mix evenly.

[0082] 4. Compression molding:

[0083] Put the magnetic powder material containing insulating agent, adhesive and release agent that has been stirred and mixed evenly into the mold, and use 18t / cm 2 pressure mo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
saturation flux densityaaaaaaaaaa
Login to View More

Abstract

The production process of soft magnetic Fe-Si-Al powder core includes the steps of compounding magnetic powder in different sizes, surface treatment, mixing magnetic powder, insulating agent, adhesive and demolding agent, molding, curing, magnetic heat treatment, soaking and surface coating. The present invention has the advantages of: breaking strength after curing in radial direction of 7-12 kg, less surface stripping, small demolding force, final breaking strength in radial direction of 17-24 kg, no influence of the insulating lacquer on electromagnetic performance and capability of realizing automatic production.

Description

technical field [0001] The invention relates to the technical field of magnetic objects, in particular to a method for manufacturing a soft magnetic silicon-aluminum magnetic powder core. Background technique [0002] At present, with the rapid development of switching power supplies and UPS, it requires magnetic components with high magnetic permeability, high saturation magnetic flux density, low loss when operating at high frequency, and a small decrease in magnetic permeability after adding a DC bias magnetic field. A large number of iron powders are used. The core generally has low magnetic permeability (for μe=75), and the core loss is relatively large. The magnetic permeability of the sendust magnetic powder core can reach μe=125, the saturation magnetic flux density is about 1.5T (Tesla), and the magnetostriction coefficient is close to zero. Now, in order to obtain a good soft magnetic silicon-aluminum magnetic powder core, use There are man...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01F1/22H01F41/02
Inventor 王锋王茜
Owner 王锋
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com