TiO2/titanium supported hydroxyapatite complex phase absorption and disinfection nano material

A titanium-loaded hydroxyapatite and hydroxyapatite technology, applied in the field of materials, can solve the problems of difficult to obtain chemically bonded hydroxyapatite composite materials, only considering the biocompatibility and antibacterial properties of the materials, and affecting the use efficiency. , to achieve the effect of high chemical stability, strong corrosion resistance and low price

Inactive Publication Date: 2005-11-30
SHANGHAI JIAO TONG UNIV
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Third, TiO 2 Photocatalysts may exhibit photocatalytic activity only when they are irradiated by ultraviolet light, which affects their use efficiency
Its shortcomings are: 1. Only consider the material biocompatibility and antibacterial properties, 2. The composite

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] x=0.05, y=0.95, z=3, TiO 2 / Titanium-loaded hydroxyapatite complex phase adsorption and disinfection nanomaterials

[0010] The material of this example is white in appearance. Tests show that its main compound is TiO in nano anatase crystal form 2 and hydroxyapatite complex. Its chemical expression is 0.05TiO 2 / {0.95(Ca7Ti 3 )(PO 4 ) 6 (OH) 2}. The material is resistant to heavy metal ions such as Pb, Cd, Cu, CO, SO 2 , NO x Harmful gases such as formaldehyde, benzene and other organic volatiles, organic dyes such as methylene blue and rhodamine, bacteria such as Escherichia coli and Staphylococcus aureus have strong adsorption capacity, and can degrade formaldehyde and methylene blue under sunlight or ultraviolet radiation. organic matter, mineralized NO x , SO x and other harmful gases, and can inactivate bacteria.

Embodiment 2

[0012] x=0.7, y=0.3, z=0.5, TiO 2 / Titanium-loaded hydroxyapatite complex phase adsorption and disinfection nanomaterials

[0013] The material of this example is white in appearance. Tests show that its main compound is TiO in nano anatase crystal form 2 and hydroxyapatite complex. Its chemical expression is 0.2TiO 2 / {0.8Ca 10 (PO 4 ) 6 (OH) 2}. The material is resistant to heavy metal ions such as Pb, Cd, Cu, CO, SO 2 , NO and other harmful gases, organic volatiles such as formaldehyde and benzene, organic dyes such as methylene blue and rhodamine, bacteria such as Escherichia coli and Staphylococcus aureus have strong adsorption capacity, and can degrade formaldehyde, Organic substances such as methylene blue can mineralize harmful gases such as NO and can inactivate bacteria.

Embodiment 3

[0015] x=0.5, y=0.5, z=1, TiO 2 / Titanium-loaded hydroxyapatite complex phase adsorption and disinfection nanomaterials

[0016] The material of this example is white in appearance. Tests show that its main compound is TiO in nano anatase crystal form 2 and hydroxyapatite complex. According to its main compound, determine the chemical expression of the material 0.5TiO 2 / {0.5(Ca 9 Ti 1 )(PO 4 ) 6 (OH) 2}. The material is resistant to heavy metal ions such as Pb, Cd, Cu, CO, SO 2 , NO and other harmful gases, organic volatiles such as formaldehyde and benzene, organic dyes such as methylene blue and rhodamine, bacteria such as Escherichia coli and Staphylococcus aureus have strong adsorption capacity, and can degrade formaldehyde, Organic substances such as methylene blue can mineralize harmful gases such as NO and can inactivate bacteria.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A sterilization material with hydroxyapatite carried TiO2 nano-power belongs to material field with its chemical composition formula is x{TiO2}/y{(Ca10-zTiz)(PO4)6(OH)2};wherein, x=0.05~0.7, y=0.3~0.95, z=0.5~3; principal crystal phase is TiO2 of anatase type and hydroxyapatite phase. By hydrothermal method obtain mentioned composite material. The product can make good use the catching function of hydroxyapatite to pollution such as virus, bacteria and organics and sterilization ability of nano-TiO2, efficient to catch and break up harmful virus and bacteria.

Description

technical field [0001] What the present invention relates to is a kind of adsorption and disinfection nanometer material, specifically, is a kind of TiO 2 / Titanium-loaded hydroxyapatite complex phase adsorption and disinfection nanomaterials. It belongs to the field of material technology. Background technique [0002] In modern life, Pb, Cd, Cu and other heavy metal ions, CO, SO 2 , NO x Harmful gases such as formaldehyde and benzene, organic dyes such as methylene blue and rhodamine, bacteria such as Escherichia coli and Staphylococcus aureus have seriously endangered human health. Photocatalytic degradation technology can be carried out under normal temperature and pressure, and can completely destroy pollutants, without secondary pollution and cost. where TiO 2 It has the advantages of good photocatalytic activity, strong corrosion resistance, high stability, relatively low price and non-toxic to human body, and is recognized as the best photocatalyst. However, fi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J20/06
Inventor 胡安民常程康李明毛大立雷同
Owner SHANGHAI JIAO TONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap