Light-degradable and biodegradable nano antibacterial plastics prepared by using waste plastics and process for preparing same

A technology of waste plastics and antibacterial plastics, which is applied in the field of controllable light-biodegradable nano-antibacterial plastics and its preparation, can solve the problems of waste and waste plastics polluting the environment, and achieve the effect of solving environmental pollution and avoiding waste of resources

Inactive Publication Date: 2005-11-30
SHENYANG INSTITUTE OF CHEMICAL TECHNOLOGY
View PDF1 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a kind of utilization waste plastics to produce controllable light-biodegradation nano antibacterial plastics and preparation method in order to solve the above-mentioned technical problem, the present inventio...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The present invention utilizes waste plastics to produce controllable photo-biodegradable nano antibacterial plastics, which consists of the following components: waste polyethylene plastic 100g, modified nano TiO 2 20g, modified starch 20g, calcium carbonate 50g, ferrocene 20g, zinc stearate 10g.

[0025] Its preparation method comprises the following process steps:

[0026] Take 80g of waste polyethylene plastics, 20g of modified starch and 50g of calcium carbonate and add them to the mixer for uniform mixing, then discharge and add to the extruder for granulation to obtain starch biodegradable masterbatch, which is set aside;

[0027] Take 10g of waste polyethylene plastic, 20g of ferrocene, and 10g of zinc stearate into a nylon bag, tighten the opening, shake, shake evenly, pour into an extruder to extrude and granulate, and then obtain photodegradable masterbatch ,spare;

[0028] Take waste polyethylene plastic 10g, modified nano-TiO 2 20g, put it into a nylon...

Embodiment 2

[0031] The present invention uses waste plastics to produce controllable photo-biodegradable nano antibacterial plastics, which consists of the following components: 200g of waste polyethylene plastics, modified nano-TiO 2 20g, modified starch 20g, calcium carbonate 50g, ferrocene 20g, zinc stearate 10g.

[0032] Its preparation method is with embodiment one.

Embodiment 3

[0034] The present invention uses waste plastics to produce controllable photo-biodegradable nano antibacterial plastics, which consists of the following components: 200g of waste polyethylene plastics, modified nano-TiO 2 1g, 10g of modified starch, 30g of calcium carbonate, 0.4g of ferrocene, 0.5g of iron stearate, 0.1g of iron dialkyldithiocarbamate.

[0035] Its preparation method is with embodiment one.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a controllable light-biodegradation nanometer antibiotic plastic and its preparation. The invention comprises waste and old vinyon, modified nanometer TiO2, modified amidon, calcium carbonate and photosensitizer. The invention reduces pollution of waste and old vinyon, avoids resource extravagant and can produce new plastic products with antibiosis and degradability.

Description

Technical field [0001] The present invention relates to a controllable light-biodegradable nano-antibacterial plastic and its preparation method, especially the use of waste plastics to organically combine the production of controllable light-biodegradation and nano-antibacterial. Biodegradable nano antibacterial plastic and its preparation method. Background technique [0002] The use of waste plastics to produce controllable light-biodegradable nano-antibacterial plastics refers to the combination of polyethylene masterbatches, antibacterial masterbatches, biodegradable masterbatches and photodegradable masterbatches made of waste plastics. The produced plastic products have dual degradability and antibacterial properties. At present, there is no similar product in China. At present, the antibacterial agent widely used in antibacterial materials is silver-based antibacterial agent. Although its bactericidal performance is high, it is easy to change color when it is expos...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L25/06
Inventor 李三喜刘旭燕周杨曲阳温祥
Owner SHENYANG INSTITUTE OF CHEMICAL TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products