Method for replacing gold stamping

A film and coating technology, which is applied in the direction of copying/marking methods, printing of special types of printed matter, and technology for producing decorative surface effects, etc., can solve problems such as low efficiency, long production cycle, and increased production cost, and achieve Simplify the traditional bronzing process, the quality of finished products is stable, and the effect of cost reduction

Inactive Publication Date: 2006-04-19
王尔健
View PDF0 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] No matter gravure printing, flat printing, flexo printing, screen printing or plateless digital printing, in order to highlight the metallic luster and luxurious and magnificent characteristics, at the same time create a strong contrast on the printed product screen, add bright colors to obtain a crystal clear eye-catching effect, especially on the packaging of cigarette labels, wine labels, gift boxes, etc., the bronzing process is generally used to achieve the effect that other processes cannot achieve at all
However, as far as the current hot stamping process is concerned, regardless of the flat pressing method, or the round pressing method, or the round pressing method, it must be cut into a single sheet, which has a long production cycle and low efficiency.
For products with large batches, although the use of gravure printing can effectively solve the problems of poor stability and low production efficiency, if the subsequent work is done with hot stamping, it will seriously restrict production efficiency, increase production costs, and deteriorate stability.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] 1. On the coating printing machine, pre-coat the transparent yellow release layer coating on the 12μPET film with the same width as the printing substrate or slightly larger, and dry and solidify;

[0017] 2. Vacuum aluminum plating in vacuum aluminum plating machine to make aluminized film;

[0018] 3. On the coating machine (or printing machine), use the designed bronzing pattern and overprint cursor line plate to coat (print) the protective layer coating, dry and solidify;

[0019] 4. In the aluminum washing tank, soak with weak alkaline water, the position coated with the protective layer coating, that is, the design bronzing pattern part, is retained, and the blank part without the protective layer coating is washed off, and then rinsed with clean water Washing, drying, film rewinding to make transfer film;

[0020] 5. On the composite machine, the transfer film is coated with composite glue and coated paper to make composite paper;

[0021] 6. On the peeling mac...

Embodiment 2

[0024] 1. On the coating printing machine, pre-coat the transparent yellow release layer coating on the 18μPET film with the same width as the printing substrate or slightly larger, and dry and solidify;

[0025] 2. Vacuum aluminum plating in vacuum aluminum plating machine to make aluminized film;

[0026] 3. On the coating machine (or printing machine), use the designed bronzing pattern and overprint cursor line plate to coat (print) the protective layer coating, dry and solidify;

[0027] 4. In the aluminum washing tank, soak with weak alkaline water, the position coated with the protective layer coating, that is, the design bronzing pattern part, is retained, and the blank part without the protective layer coating is washed off, and then rinsed with clean water Washing, drying, film rewinding to make transfer film;

[0028] 5. On the gravure printing machine of the composite machine, the transfer film is coated with composite glue and white cardboard to make a composite p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A substitute method for gilding includes such steps as coating the parting paint on PET film, baking for solidifying, vacuum aluminizing, coating protecting paint with gilding pattern plate, baking for solidifying, immersing in alkali solution for removing aluminium, baking to obtain transfer film, coating adhesive, sticking onto substrate to obtain composite paper, stripping the film to obtain transfer paper, and printing with said transfer paper.

Description

technical field [0001] The invention belongs to a method for replacing bronzing, and in particular relates to a method for replacing bronzing by adopting an aluminum washing process to make transfer paper and using a film printing aluminum process for composite printed matter. Background technique [0002] The traditional bronzing process is: using anodized aluminum (also metal foil, powder, color foil, etc., but currently the most important is anodized aluminum) material, pre-engraving the pattern to be hot stamped on the hot stamping plate, when the hot stamping plate with the When the heating plate is heated up to a certain temperature, the anodized aluminum film and the substrate are imprinted, and the adhesive layer, metal aluminum layer and color layer attached to the anodized aluminum film are transferred to the substrate by the action of temperature and pressure. , forming bright, rich metallic effect patterns. [0003] No matter gravure printing, flat printing, fle...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B44C1/165B41M3/12B41M5/00
Inventor 王尔健白鹏飞王重声陈继东孔繁辉赵志敏徐军
Owner 王尔健
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap