Adhesive for preparing iron powder ball using iron ore powder and its prepared ironpowder ball

A binder and iron ore powder technology, applied in the field of blast furnace ironmaking in the metallurgical industry, can solve problems such as increasing ironmaking costs, achieve good oxygen and heat permeability, high strength, and reduce energy consumption

Inactive Publication Date: 2006-06-14
姜文平 +1
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the high-temperature sintering process increases the cost of ironmaking

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Embodiment 1 Get each component of binder by following parts by weight and mix uniformly to obtain iron ore powder binder:

[0029] 70 parts of water glass saturated solution

[0030] Aluminum Potassium Sulfate 8 parts

[0031] 12.5 parts of boron tetroxide

[0032] Sulfur 7.5 parts

[0033] Diffuser OP-10 0.4 parts

[0034] 20 parts of water

[0035] Take iron ore powder with iron content of 50% by weight, 92% iron ore powder and 8% binder, stir and mix the two, and use a ball press to press the mixture into a wet ball with a diameter of 3 to 6 cm. Dry the iron powder ball at room temperature to obtain a higher strength iron powder ball.

[0036] The specification is 35m 3 The hot air furnace is used as iron-making equipment to smelt the prepared iron powder balls. The iron powder balls are continuously put into the warm air furnace, and the temperature is gradually raised to the smelting temperature of 1700°C, and hydrogen and oxygen are blown into the furnace. ...

Embodiment 2

[0040] Embodiment 2 Get each component of binder by following parts by weight and mix uniformly to obtain iron ore powder binder:

[0041] 80 parts of water glass saturated solution

[0042] Aluminum Potassium Sulfate 8 parts

[0043] 12.5 parts of boron tetroxide

[0044] Sulfur 8.5 parts

[0045] Diffusion agent MF 0.4 parts

[0046] 25 parts of water

[0047] Take the iron ore powder with iron content of 63% by weight, 92.5% iron ore powder and 7.5% binder, stir and mix the two, and press the mixture into a wet ball with a ball diameter of 3 to 6 cm. Dry the iron powder ball at room temperature to obtain a higher strength iron powder ball.

[0048]The specification is 35m 3 The hot air furnace is used as iron-making equipment to smelt the prepared iron powder balls. The iron powder balls are continuously put into the warm air furnace, and the temperature is gradually raised to the smelting temperature of 1700°C, and hydrogen and oxygen are blown into the furnace. Afte...

Embodiment 3

[0049] Embodiment 3 Get each component of binder by following parts by weight and mix uniformly to obtain iron ore powder binder:

[0050] 80 parts of water glass saturated solution

[0051] Aluminum Potassium Sulfate 9 parts

[0052] Boron tetroxide 10 parts

[0053] Sulfur 7.5 parts

[0054] Diffusion agent Pingping plus O-10 0.5 parts

[0055] 25 parts of water

[0056] Get iron ore powder with iron content of 44% by weight, 92.5% iron ore powder by weight, and 7.5% binder to stir and mix the two, and use a ball press to press the mixture into a wet ball with a ball diameter within the range of 3 to 6 cm. Dry the iron powder ball at room temperature to obtain a higher strength iron powder ball.

[0057] The specification is 35m 3 The hot air furnace is used as iron-making equipment to smelt the prepared iron powder balls. The iron powder balls are continuously put into the warm air furnace, and the temperature is gradually raised to the smelting temperature of 1700°C,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an iron ore powder preparing iron powder ball bonding agent and the iron powder ball. It belongs to metallurgy industry blast furnace iron making technique field. The bonding agent material and its amounts by weight are water glass saturated solution 70-80, potassium aluminum sulfate 8-9, tetra-boron oxide 10-15, sulfur 7.5-8.5, organic dispersing agent, and water 20-25. The preparing method mixing the bonding agent and the iron ore powder by weight; using ball press to form iron powder wet ball with 3-6cm diameter; naturally drying to gain iron powder ball. The bonding agent makes the iron powder ball have good high temperature sphericity and intension without agglomeration to reduce preparing cost, makes the iron powder have good oxygen permeability and diathermancy to reduce energy consumption. The invention can apply in various iron powder preparing iron powder ball and blast furnace iron making.

Description

technical field [0001] The invention belongs to the technical field of blast furnace ironmaking in the metallurgical industry, and in particular relates to an iron powder ball prepared from iron ore powder for ironmaking and a binder for preparing the iron powder ball. Background technique [0002] Iron ore powder is prepared into iron pellets during blast furnace ironmaking, which can optimize the structure of blast furnace charge, improve the oxygen and heat permeability of iron ore powder, and reduce energy consumption. Because high-grade iron ore powder is agglomerated with an organic binder, the hot and cold strength is low, and it is easy to pulverize in the smelting furnace, which is not conducive to smelting. At present, the inorganic binder materials used in the preparation of iron pellets include bentonite, coke powder, etc. Coal derivatives and nitric acid, etc., the organic binders used include guar gum, vinyl monomer, lignosulfonate, etc. Although the inorganic ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22B1/242
Inventor 姜文平
Owner 姜文平
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com