Hard alloy composite roll collar for high-speed wire production line and method for manufacturing the same

A technology of cemented carbide and composite rolls, which is used in metal rolling, manufacturing tools, metal rolling, etc. to achieve the effects of good performance, improved service life, and improved wear resistance.

Inactive Publication Date: 2006-10-11
宣化盛龙冶金设备制造厂 +2
View PDF0 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to overcome the shortcomings that the existing roller rings cannot meet the requirements of hardness and wear resistance of the working layer and the existing production technology cannot realize the recycling of scrapped roller rings, the purpose of the present invention is to provide a high-strength hard roller ring. Alloy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hard alloy composite roll collar for high-speed wire production line and method for manufacturing the same
  • Hard alloy composite roll collar for high-speed wire production line and method for manufacturing the same
  • Hard alloy composite roll collar for high-speed wire production line and method for manufacturing the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0037] Below in conjunction with accompanying drawing and embodiment the present invention is further described:

[0038] image 3 Shown is an embodiment of the high-wire cemented carbide composite roll ring of the present invention, B in the figure represents the composite working layer, and C represents the matrix part of the composite roll ring. The workpiece specification is Φ228.3mm, the hardness of the working layer B is 87HRA, and the density is 14.3 / cm3 tungsten carbide powder, and the tungsten carbide material of the roller ring base C has a hardness of 85HRA and a density of 13.9g / cm 3 The double-grade materials are sintered into one body through a composite process, and then processed into a composite roller ring by grinding. For another example, the workpiece specification is Φ168.66mm, the hardness of the tungsten carbide cemented carbide material of the roller ring base is 85HRA, and the density is 13.9g / cm 3 , the working layer tungsten carbide hard alloy mate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a high-liner rigid alloy compound roll collar, which comprises a base and a compound working layer whose material brand is different to the base while they are sintered into one whole. The producing method comprises: filling the base and the rigid alloy powder of non-doping molding agent into graphite mould; via vibration, they are filled into special middle-frequency hydraulic vibrating sintering device to be thermally compressed and sintered; and processing second positive pressure sintering; checking the quality and grinding to attain the final product. The invention can improve the rigidity of working layer and the friction resistance; improve the rolling amount of roll collar and the service life, while the waste roll collar can be recycled to save metallic resource. It can apply the finisher of high-speed producing line whose rolling speed reaches 100m/s.

Description

technical field [0001] The invention relates to a roll ring for a finishing mill suitable for a high-speed wire rolling production line and a manufacturing process thereof, belonging to the technical field of cemented carbide powder metallurgy. Background technique [0002] Existing primary roller rings such as figure 1 As shown, after the user unit opens a groove for rolling wire rod on the outer circle of the roll ring according to the production needs, it is installed on the finishing rolling unit (more than a dozen shelves) and used in pairs. During production, due to high temperature, high speed and high pressure, the roller ring is worn, and the roller ring should be frequently ground off-line to grind the groove shape and outer diameter. When the outer diameter is ground to the specified size (more than ten times of grinding, the weight will be reduced by about 30%) .The continuous service life is about 60 days) and it will be scrapped offline, see attached figure ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B21B27/02B22F7/04
Inventor 吴峻
Owner 宣化盛龙冶金设备制造厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap