High-alkalization degree poly-ion polymerized composite coagulant and preparation method thereof

A technology of alkalinity and polyion, applied in the direction of flocculation/sedimentation water/sewage treatment, etc., can solve the problems of limitation, low content of heavy metal impurities, high product cost, and achieve the effect of reducing maintenance costs, improving conversion rate and saving energy.

Inactive Publication Date: 2006-10-11
CHANGCHUN WATER GROUP
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The product not only has good appearance, low content of heavy metal impurities, but also has excellent flocculation effect, but the product cost is high. For the economically underdeveloped country, the application and promotion of its products in China will inevitably be restricted.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Weigh aluminum hydroxide: 1.366 tons; hydrochloric acid: 6.898 tons, heat up to 130°C, pressure 0.15MPa, and react for 2 hours. Add 5.09 tons of water to the reaction tank, add the above-mentioned feed liquid, the temperature should be between 70-90°C, add 2.40 tons of calcium powder for reaction, when the viscosity of the reaction feed liquid reaches 102-103mPa·S, some water can be added Dilute and continue to react. When the viscosity of the feed liquid reaches the initial viscosity again, add some water to dilute again, and repeat this for 2 to 3 times until the viscosity of the feed liquid reaches between 10mPa·S and 300mPa·S, and the viscosity of the feed liquid no longer continues Finally, add all the remaining 3.5 to 4.5 tons of water into the feed liquid at one time, and this process should be completed within 2 hours. A total of 5.8 tons of water was added during the reaction, and the temperature of the feed liquid after adding calcium powder should be kept bet...

Embodiment 2

[0021] Weigh aluminum hydroxide: 1.466 tons; hydrochloric acid: 6.40 tons, heat up to 150°C, pressure 0.20MPa, and react for 1.5 hours. Add 4.50 tons of water to the reaction tank, add the above-mentioned feed liquid, the temperature should be between 70-90°C, add 2.50 tons of calcium powder for reaction, when the viscosity of the reaction feed liquid reaches 102-103mPa·S, add some water Dilute and continue to react. When the viscosity of the feed liquid reaches the initial viscosity again, add some water to dilute again, and repeat this for 2 to 3 times until the viscosity of the feed liquid reaches between 10mPa·S and 300mPa·S, and the viscosity of the feed liquid no longer continues Finally, add all the remaining 4 to 5 tons of water into the feed liquid at one time, and this process should end within 1.5 hours. A total of 6.50 tons of water was added during the reaction, and the temperature of the feed liquid after adding calcium powder should be kept between 50 and 70°C. ...

Embodiment 3

[0023] Weigh aluminum hydroxide: 1.628 tons; hydrochloric acid: 6.4 tons, add 4.8 tons of water to the reaction tank, add the above-mentioned liquid, the temperature should be between 70 ~ 90 ° C, add 2.60 tons of calcium powder for reaction, when the reaction material When the viscosity of the liquid reaches 102-103mPa·S, add part of water to dilute and continue the reaction. When the viscosity of the material liquid reaches the initial viscosity again, add part of water to dilute again, and repeat this for 2-3 times until the viscosity of the material liquid reaches 10mPa·S Between ~300mPa·S, until the feed liquid is no longer viscous, finally add all the remaining 5-6 tons of water into the feed liquid at one time, and this process should end within 1.5 hours. A total of 7.0 tons of water was added during the reaction, and the temperature of the feed liquid after adding calcium powder should be kept between 50 and 70°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a manufacturing technique of multiple ion complexing coagulant of overbasification polymerization, which comprises the following steps: adding aluminum hydroxide and hydrochloric acid in proportion into autoclave, reacting for 1-3 hours with the condition of 100-200 DEG C, 0.10-0.4Mpa, adding water and calcium aluminate powder in proportion, when reaction feed liquid becomes viscous, diluting it with water until it isn't viscous, keep on reacting, when becoming viscous again, adding water again for dilution until it doesn't become viscous any more, finally, adding surplus water into feed liquid one time, to get the product at the end of reaction. By controlling indexes such as temperature, viscosity to make it reach to optimum state of polymerization, it has special configuration state. It not only has the merits of strong adsorption charge neutrality, coagulation, binding bridging, avoiding adjusting PH values of overbasification coagulant, but also compared with other coagulant, it obviously improves the quality of water outlet, and decreases cost of expenses.

Description

technical field [0001] The invention provides a high alkalization degree polymerized multi-ion silicon-aluminum-calcium chloride composite coagulant and a preparation method thereof, belonging to the technical field of preparation of chemical reagents for flocculation water treatment. Background technique [0002] At present, most manufacturers usually use aluminum-containing raw materials, such as bauxite, calcium aluminate powder and other raw materials to react with acid products, and adjust the ratio of raw materials, reaction temperature, time or pressure to achieve the best reaction state of the product. In terms of the application effect of the product, due to the influence of the morphological structure, the unit consumption of the existing product is relatively high, which not only increases the cost of water treatment, but also affects some metal elements in the water, especially the content of heavy metal elements and residual aluminum content In the field of drin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C02F1/52
Inventor 历建萍姜万林马平程秀本杨天栋
Owner CHANGCHUN WATER GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com