A floor material and inorganic technology, applied in the field of floor materials, can solve problems such as difficult to meet the use requirements of the floor, easy cracking, sanding, etc., and achieve the effects of high strength index, excellent waterproof performance, and good wear resistance

Inactive Publication Date: 2006-12-06
SHANDONG ZERUI NEW MATERIAL TECH
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The currently used floor materials are only materials such as cement, sand and a small amount of additives for mixing and mixing. The disadvantages are that they are easy to crack, dust, and sand, and it is difficult to meet the floor requirements of factories, laboratories, offices, and living rooms.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0009] The powder in the formula uses a double-helix conical mixer. First add cement and fine sand to the mixer, start the machine, and mix for 5-10 minutes, then add other fillers, continue mixing for 5-10 minutes, and observe whether the color and interface are It has been mixed evenly. If you think it is not uniform, you can continue to prolong the mixing time. Finally, add cellulose, etc., continue mixing for 5-10 minutes, and finally put the material into a woven bag lined with waterproof and moisture-proof plastic film, and seal the bag mouth to prevent Damp water, ready to use.

[0010] Liquid polymer emulsion, put it into a plastic or iron bucket of a specific volume, seal it, open it on site, pour it into a mixing bucket, use an electric mixer according to the formula ratio, and stir it until it is uniform. According to the temperature and construction requirements, you can add water in an appropriate amount Adjust the consistency of the bonding mortar.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle size (mesh)aaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

This invention relates to a self-leveling inorganic floor material. The material is composed of cement 50-100 wt. parts, sand 200-400 wt. parts, and heavy weight calcium carbonate 100-300 wt. parts. The material is also composed of tackiness agent 10-20 wt. %, polymer emulsion 10-30 wt. %, and water reducer 0.7 wt. %. The material can be used for retarding floors, and has such advantages as high adhesiveness, high water resistance, and good waterproof effect. The material can be manufactured into floors with different colors, and used in moisture environment.

Description

technical field [0001] The invention relates to a floor material, in particular to an inorganic self-flowing renovation floor material. Background technique [0002] The currently used floor materials are only materials such as cement, sand and a small amount of additives that are stirred and mixed. The disadvantages are that they are easy to crack, dust, and sand, and it is difficult to meet the floor requirements of factories, laboratories, offices, and living rooms. Contents of the invention [0003] The object of the present invention is to provide an inorganic artesian refurbishment floor material suitable for renovation of old ground against the defects of the prior art. [0004] The technical proposal is: main raw materials including the following parts by weight: 50-100 parts of cement, 200-400 parts of sand, 100-300 parts of heavy calcium carbonate, and auxiliary materials accounting for the weight percentage of the whole material: 10-20% of tackifier, polymer It...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B14/06C04B14/28C04B24/38C04B24/24C04B24/20
CPCC04B2111/62C04B2111/27C04B28/02
Inventor 李广志夏文强钟涛
Owner SHANDONG ZERUI NEW MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products