Soft tin-plate of hardness HR30T 51+/-3 and its making process

A manufacturing method and technology of tinplate, applied in the direction of manufacturing tools, metal rolling, metal rolling, etc., can solve the problems of difficult stable control of hardness and large variation range of thickness specifications

Active Publication Date: 2007-01-03
BAOSHAN IRON & STEEL CO LTD
View PDF0 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the wide range of thickness specifications, it

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1-6

[0045] Example 1-6: Production of thicker (>0.25mm) T-1.5 soft tinplate using titanium-IF steel. The molten steel is vacuum degassed by RH refining, and a variety of measures to control inclusions are adopted. Finally, the continuous casting slab is produced by the conventional continuous casting process. The chemical composition of the molten steel is shown in Table 2, and the steel also contains other unavoidable impurities. elements, the balance being Fe.

[0046]

make up

No

finished product

thickness

(mm)

C

Si

mn

P

S

Al

N

O

Ti

1

0.26

0.0050

0.007

0.26

0.010

0.0065

0.045

0.0026

0.0027

0.060

2

0.28

0.0040

0.015

0.28

0.012

0.0055

...

example 7-12

[0053] Example 7-12: Using titanium-IF steel to produce thin gauge tinplate with a thickness less than or equal to 0.25mm. The molten steel was treated by RH refining vacuum degassing, and various measures to control inclusions were adopted. Finally, the continuous casting slab was produced by the conventional continuous casting process. The chemical composition of the molten steel is shown in Table 6, and the steel also contains other unavoidable impurities. elements, the balance being Fe.

[0054] make up

No

finished product

thickness

C

Si

mn

P

S

Al

N

O

Ti

7

0.23

0.0015

0.025

0.23

0.009

0.0150

0.060

0.0023

0.0040

0.045

8

0.25

0.0020

0.006

0.28

0.012

0.0100

0.030

0.0020

0.0021

0.042

9

0.17

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The soft tin-plate of hardness HR30T 51+/-3 consists of C not more than 0.005 wt%, Mn 0.20-0.30 wt%, Al 0.03-0.06 wt%, Si not more than 0.03 wt%, Ti 0.03-0.06 wt%, P not more than 0.012 wt%, S not more than 0.015 wt%, N not more than 0.003 wt%, O not more than 0.004 wt%, and Fe and inevitable impurities for the rest. Its production process includes the following steps: smelting steel, continuous casting and rolling, hot rolling, acid pickling and rolling, continuous annealing, flattening and tin plating.

Description

technical field [0001] The invention relates to a soft tinplate and a manufacturing method thereof, in particular to a soft tinplate with a hardness HR30T within 51±3 and a manufacturing method thereof. The soft tinplate is produced by continuous annealing of titanium-IF steel , mainly used for the production of flower basket barrels with enlarged diameters, can lids with complicated deformation and stamped and deformed cans. Background technique [0002] The production technology of tinplate is relatively mature and well known. With the expansion of the scope of use of tinplate, soft tinplate with excellent formability and hard tinplate with thin specifications have become the two main directions of its development. . [0003] According to the Japanese Industrial Standard JIS G3303, the hardness range of different grades of tinplate is shown in Table 1. Among them, T-1 to T-3 are soft tinplates, and T-4 to T-6 are hard tinplates. [0004] level HR30T hardnes...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/14B21B1/46B21B37/00C21D9/46
CPCC22C38/14C22C38/004C22C38/02C22C38/06C22C38/04
Inventor 李俊林秀贞张理扬金仁忠
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap