Manufacture method of high electric superalloy conductor and product thereof

A technology of aluminum alloy wire and manufacturing method, applied in the direction of metal/alloy conductor, etc., can solve the problems of small increase in capacity, increase in sag, increase in wire temperature, etc.

Active Publication Date: 2007-03-07
QINGDAO HANHE CABLE
View PDF0 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the heat-resistant wires used in my country's urban and rural power transmission and transformation lines are generally twisted from ordinary heat-resistant aluminum alloy single wires and ordinary galvanized steel wires. The aluminum alloy wire generally has a long-term operating temperature of no more than 150°C, which can only increase the carrying capacity by 1.6 times compared with ordinary wires, and the increase in capacity is not large. However, the ordinary galvanized steel wire used as a strengthening element has a large linear expansion coefficient after preheating, and the transmission capacity After the increase, the temperature of the wire rises and the sag increases, which affects the safe operation of the line

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Test items

[0016] Then, 7 Φ3.2 galvanized invar wires are twisted together to form a GCNRLH60GJ-240 / 55 high-conductivity super-heat-resistant aluminum alloy wire, G-means high conductivity, C-super heat-resistant, N-heat-resistant, LH-aluminum alloy, 60-conductivity 60% IACS, G-steel wire J-stranded wire.

Embodiment 2

[0018] Test items

[0019] Then, 7 Φ3.07 galvanized invar wires are twisted together to form a GCNRLH60GJ-400 / 50 high-conductivity super-heat-resistant aluminum alloy wire.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparing method of high-conductive thermal tolerance aluminum alloy wire, which comprises the following steps: 1. adding Zr and Fe in the electric aluminium liquid (0.3-0.6% Zr, 0.10-0.25 Fe, not more than 0.08% Si, not more than 0.01% element sum of Ti, V, Mn and Cr); 2. manufacturing thermal tolerance aluminium alloy rod material through continuous aluminium casting manufacturing line; 3. setting the heading temperature at 400-430 deg.c for 50h; 4. drawing and stranding to manufacture high-conductive thermal tolerance alloy wire.

Description

Technical field [0001] The invention relates to a method for manufacturing an aluminum alloy wire, in particular to a method for manufacturing a high-conductivity super-heat-resistant aluminum alloy wire used in overhead power transmission and transformation lines and products produced by the method. Background technique [0002] At present, the heat-resistant wires used in my country's urban and rural power transmission and transformation lines are generally twisted from ordinary heat-resistant aluminum alloy single wires and ordinary galvanized steel wires. The aluminum alloy wire generally has a long-term operating temperature of no more than 150°C, which can only increase the carrying capacity by 1.6 times compared with ordinary wires, and the increase in capacity is not large. However, the ordinary galvanized steel wire used as a strengthening element has a large linear expansion coefficient after preheating, and the transmission capacity After the increase, the temperatu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/00C22C1/02C22F1/04H01B1/02
Inventor 陈沛云赵新院
Owner QINGDAO HANHE CABLE