Flame-proof polystyrene composition and its preparation method

A technology of polystyrene and polystyrene resin is applied in the field of flame retardant polystyrene composition and its preparation, and can solve the problems of low flame retardant efficiency, large amount of flame retardant added, and low flame retardant grade of flame retardant materials. , to achieve the effect of high flame retardant efficiency, less addition, and good flame retardant effect

Inactive Publication Date: 2007-05-23
BEIJING INSTITUTE OF TECHNOLOGYGY
View PDF0 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the existing halogenated flame-retardant polystyrene technology has the following problems: a large amount of flame re

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～7

[0028] High-impact polystyrene resin, halogenated flame retardant (a mixture of decabromodiphenylethane and heat-stable hexabromocyclododecane or brominated polystyrene), antimony trioxide and composite antioxidant (The mixture of antioxidant 1010 and antioxidant 168) is mixed at high speed in a high-speed mixer to make the materials fully mixed. Put the mixed material into the twin-screw extruder, the screw rotation speed is 300r / min, and the temperature of the first to seventh zones on the extruder is 175°C, 185°C, 185°C, 185°C, 180°C, 180°C, 165°C (machine Head) under the conditions of melt extrusion, granulation.

[0029] The obtained pellets were put into an oven and dried at 80° C. for 8 hours, and then injection molded into standard splines with an injection molding machine. The injection molding temperature was set at 195°C. The standard splines were tested for various mechanical properties, and the results are shown in Table 1. The amount of the raw materials is ba...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a fire-retardant polystyrene combination and its preparation method. involving flame-retardant resin modification field. The said combination contains (weight parts) polystyrene 100, halogen flame-retardant 8~25, and synergistic flame retardant 2~6. The halogen flame retardant is brominated polystyrene or a mixture of decabrominated dipheny ethane and hexabromocyclododecane with thermal decomposition temperature greater than or equal to 200degreeC, wherein the ratio of decabrominated dipheny ethane to hexabromocyclododecane is at 2 : 1 ~ 1 : 2. The synergistic flame retardant is antimony trioxide. The combination is prepared by mixing and melting the above materials with good fire-retardant properties, flame retardant level up to FV-0 level (GB/T4609-93) and the oxygen index up to 28, which can be applied to various adverse circumstances.

Description

Technical field: [0001] The invention relates to a flame-retardant polystyrene composition, and furthermore, relates to a flame-retardant polystyrene composition modified with a halogen flame retardant and a preparation method thereof. Background technique: [0002] At present, most of the halogenated flame retardants of polystyrene are mainly brominated flame retardants. Considering the increasing requirements for flame retardant efficiency and environmental indicators of flame retardants, flame retardants used for polystyrene at home and abroad mainly include decabromodiphenyl ether, decabromodiphenylethane, tetrabromobisphenol A, etc. The flame retardant system is composed of antimony synergistic flame retardants. For example, Mr. Quan Ying from the Institute of Polymer Science of Tsinghua University and Mr. Yang Mingshan from the Institute of Physics and Chemistry of the Chinese Academy of Sciences developed low-smoke, flame-retardant, high-impact polystyrene by adding ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L25/06C08K5/524C08K3/22C08K5/03C08K5/36
Inventor 焦清介臧充光杨化浩吴中伟刘帅
Owner BEIJING INSTITUTE OF TECHNOLOGYGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap