Alumium Foil for air conditioner

A technology for air conditioners and aluminum foils, applied in the direction of metal rolling, etc., can solve the problems of slow punching speed, film rewinding, poor processability, etc., and achieve moderate strength, high elongation and cupping value, and good processability. Effect

Inactive Publication Date: 2007-06-06
JIANGSU DINGSHENG NEW MATERIAL JOINT STOCK CO LTD
View PDF1 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The quality of aluminum foil for household air conditioners, refrigerators and automobile air conditioners depends on the ratio of raw materials and the refining process. The patent number is 02138192.5, and the patent name is "a kind of aluminum foil and its production method". The aluminum foil produced by this patent method is used in actual use. There are still punching and cracking phenomena, and there is a phenomenon of rewinding in the bending process, and the punching speed is slow. The reason is that the composition of the raw materials and the process cannot completely change the internal structure of the aluminum foil, resulting in poor formability.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0006] Example 1: Prepare raw materials according to the following parts by weight: Al: 99.485 parts; Fe: 0.15 parts; Si: 0.08 parts; Mn: 0.20 parts; Mg: 0.005 parts; Zn: 0.005 parts; Cu: 0.05 parts; Ti: 0.01 Parts; Ni: 0.01 parts; Cr: 0.005 parts. The above-mentioned raw materials are operated in sequence as follows: (1) Put the weight parts of raw materials into a smelting furnace, smelting and refining at 700 and 735°C respectively to make aluminum melt; (2) At 685 At temperature, use a continuous casting and rolling cast-rolling mill to cast-roll the above-mentioned aluminum melt to a thickness of 6.0-8.0mm thick cast-rolled coil; (3) Use a cold rolling mill to cold-roll the cast-rolled coil to a 0.6mm thick aluminum coil; (4) After cutting the edges in the middle, continue to cold-roll the aluminum foil to a thickness of 0.08~0.2mm; (5) Put the aluminum foil in step (4) into an electric furnace at a temperature of 240℃, anneal for 24 hours, take it out, and cool to room tempe...

Embodiment 2

[0007] Example 2: Prepare raw materials according to the following parts by weight: Al: 99.36 parts; Fe: 0.20 parts; Fe: 0.12 parts; Mn: 0.22 parts; Mg: 0.03 parts; Zn: 0.01 parts; Cu: 0.01 parts; Ti: 0.04 parts Parts; Ni: 0.005 parts; Cr: 0.005 parts. The above-mentioned raw materials are operated in sequence as follows: (1) Put the weight of the raw materials into the melting furnace, and respectively smelt and refine them at 730°C and 745°C to form an aluminum melt; (2) In At a temperature of 690℃, the above-mentioned aluminum melt is cast-rolled into a cast-rolled coil with a thickness of 6.0~8.0mm with a continuous casting and rolling cast-rolling machine; (3) The cast-rolled coil is cold-rolled to a thickness of 0.6mm with a cold rolling mill. Roll; (4) After cutting the edges in the middle, continue to cold-roll to 0.08~0.2mm aluminum foil; (5) Put the aluminum foil in step (4) into an electric furnace at a temperature of 280℃, anneal for 28 hours, take it out, and cool To ...

Embodiment 3

[0008] Example 3: Prepare raw materials according to the following parts by weight: Al: 99.30 parts; Fe: 0.26 parts; Si: 0.16 parts; Mn: 0.25 parts; Mg: 0.01 parts; Zn: 0.005 parts; Cu: 0.001 parts; Ti: 0.008 Parts; Ni: 0.001 parts; Cr: 0.005 parts. The above raw materials are operated in sequence as follows: (1) Put the weight parts of raw materials into a smelting furnace, smelting and refining at 760°C and 750°C respectively to make an aluminum melt; (2) In At 700℃, the above-mentioned aluminum melt is cast-rolled into a cast-rolled coil with a thickness of 6.0~8.0mm with a continuous casting and rolling-casting mill; (3) The cast-rolled coil is cold-rolled to a thickness of 0.6mm with a cold rolling mill. Roll; (4) After the middle trimming, continue to cold-roll to 0.08~0.2mm aluminum foil; (5) Put the aluminum foil in step (4) into an electric furnace at a temperature of 300°C, anneal for 33 hours, take it out, and cool To room temperature, (6) cut the annealed aluminum foil...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The present invention discloses one kind of aluminum foil for air conditioner and refrigerator. The aluminum foil is produced with the materials including Al 99-99.50 weight portions, Fe 0.15-0.28 weight portion, Si 0.08-0.18 weight portion, Mn 0.20-0.25 weight portion, Mg <0.05 weight portion, Zn <0.1 weight portion, Cu <0.1 weight portion, Ti <0.08 weight portion, Ni <0.05 weight portion, and Cr <0.05 weight portion, and through smelting, casting and rolling, cold rolling, annealing and other steps. The aluminum foil has homogeneous structure, high elongation and cupping value, moderate strength, and excellent machining and forming performance, and is especially suitable for punching in a high speed punch.

Description

Technical field [0001] The invention relates to aluminum foil for refrigeration equipment such as household air conditioners, refrigerators, and automobile air conditioners. Background technique [0002] The quality of aluminum foil for household air conditioners, refrigerators, and automobile air conditioners depends on the ratio of raw materials and the refining process. The patent number is 02138192.5, and the patent name is "An aluminum foil and its production method". The aluminum foil produced by this patented method is actually used There are still punching and cracking phenomenon, rewinding phenomenon in the bending process, and the punching speed is slow. The reason is that the composition and process of the raw material can not completely change the internal structure of the aluminum foil, resulting in poor processing and formability. Summary of the invention [0003] In order to overcome the shortcomings of the prior art, the present invention provides an aluminum foi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/00C22C1/02B21B1/40B21B1/46C21D1/04
Inventor 刘倜刘文彬
Owner JIANGSU DINGSHENG NEW MATERIAL JOINT STOCK CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com