Railroad steels having improved resistance to rolling contact fatigue

Abstract

Steels having a pearlitic structure and containing 0.6 to 0.8 wt. % carbon; 0.70 to 1.00 wt. % silicon and 0.8 to 1.2 wt. % manganese can be further alloyed with chromium, molybdenum, vanadium, niobium and / or copper and used to make railway wheels, railway rims and railway rails that are particularly resistant to rolling contact fatigue and, hence, shelling.

Description

BACKGROUND OF THE INVENTION[0001]1. Field of the Invention[0002]The present invention generally relates to railroad steels. It is especially concerned with railroad steels that are alloyed and / or heat treated to make railroad wheels that resist both wear and thermo-mechanical deterioration, especially in the tread (and / or flange) regions of such wheels. The terms “spalling” and “shelling” are widely used in describing such thermo-mechanical deterioration. Spalling generally refers to loss of wheel tread material as a result of metallurgical damage created by excessive heat that results from sliding of railroad wheels during train braking operations. Shelling generally refers to loss of wheel tread material as a result of deterioration arising from mechanical stresses.[0003]Various problems arise from each form of tread material loss. By way of example only, thermo-generated deterioration of a railroad wheel's tread can quickly create flat spots on the wheel's outer surface and there...

AI Technical Summary

Benefits of technology

[0059]As far as alloying element differences between Applicants' steels and those steels taught by the '635 patent are concerned, Applicants employ niobium, nickel, molybdenum and vanadium. These elements are not taught or suggested by t

Problems solved by technology

Steel railroad wheels eventually wear out as a result of normal usage.

Such wheels are however often prematurely forced from service as a result of various forms of thermo-mechanical deterioration.

A great deal of the thermo aspect of thermo-mechanical deterioration results from metallurgical transformation of a railroad wheel's tread / flange steel from its original, relatively tough, pearlitic structure to more brittle structures such as austenite, bainite and / or martensite—with attendant loss of the bainite / martensite materials through spalling.

Again, thermo deterioration is caused by the heat generated by friction when a train's wheels skid during braking operations.

Wheel skids can damage the rails as well.

In any case, the resulting brittle martensite material then tends to crack and fall away from the wheel.

That is to say that rolling contact fatigue can occur even if the tread steel does not experience metallographic changing temperatures.

Rolling contact fatigue is generally caused by diminished shear fatigue strength of the wheel's tread surface steel.

In any case, rolling contact fatigue is related to both the strength of the wheel tread surface and to the load applied to it.

These relatively greater loads lead directly to higher levels of rolling contact fatigue.

The use of hard steels notwithstanding, railroads are experiencing an increasing incidence of shelling type defects in freight car wheels as a result of the greater loads they are currently being called upon to carry.

Driving forces tend to cause cracks in a wheel's flange regions while normal loads tend to cause shelling of the tread.

Moreover, when brake heated wheels again cool, residual tensile stresses may remain therein and subsequently serve to open any surface cracks that may be present.

The rails in such regions experience relatively greater wear and / or damage as well.

For example, elevated temperatures in a wheel steel serve to reduce its ability to resist mechanical loading owing to the steel's diminished mechanical strength above certain temperatures and / or levels.

Moreover, the longer a wheel steel experiences elevated temperatures, the greater the degree of shelling that will result from this time related circumstance.

Unfortunately, to varying degrees, these properties range from being metallurgically antagonistic to being metallurgically incompatible.

Conversely, when a steel is alloyed to be more resistant to thermo-generated deterioration, this usually implies that the steel will be less hard, and hence, inherently less wear resistant.

Such steels are not, however, particularly resistant to thermo-mechanical deterioration.

It should be appreciated however that some custom based statements can lead to misunderstandings.

This all goes to say that the wear resistance versus thermo-mechanical resistance problem has a persistent dilemmatic quality that continues to thwart the railroad industry's attempts to extend the useful life of railway wheels, rims and rails.

Heat producing wheel skids on the other hand are relatively unpredictable.

Worse yet, thermo-generated deterioration tends to produce damage that is much more immediate and much more severe in nature.

Thus far, alloying theories have been of somewhat limited value in dealing with the wear resistance vs. thermo-mechanical deterioration dilemma.

For example, even though the constitution of three component steels can theoretically be deduced from ternary phase diagrams, they are often rather difficult to interpret.

Their practical value is also limited by the fact that they only describe equilibrium conditions.

Therefore, since most modern railroad wheel steels are both heat treated during their manufacture and contain more than three alloying components, much more complex graphing methods (e.g., Temperature Time Transformation diagrams) must be employed and interpreted—thus far with varying degrees of success as far as railroad steels are concerned.

Further complexities arise from various heat treatment processes to which most steels are usually exposed.

Unfortunately, however, many martensite transformation conditions produced by the heat generated by heavy braking conditions do not coincide with the martensite transformation conditions that can be avoided in highly controlled manufacturing processes such as those disclosed in the '516 patent.

Indeed, rolling contact fatigue problems are becoming more and more pronounced as freight cars are increasingly being called upon to carry maximum allowable loads.