Laser Based Metal Deposition LBMD of Antimicrobials to Implant Surfaces

Abstract

A method is provided for depositing a hard wear resistant surface onto a porous or non-porous base material of a medical implant. The wear resistant surface of the medical implant device may be formed by a Laser Based Metal Deposition (LBMD) method such as Laser Engineered Net Shaping (LENS). The wear resistant surface may include a blend of multiple different biocompatible materials. Further, functionally graded layers of biocompatible materials may be used to form the wear resistant surface. Usage of a porous material for the base may promote bone ingrowth to allow the implant to fuse strongly with the bone of a host patient. The hard wear resistant surface provides device longevity, particularly when applied to bearing surfaces such as artificial joint bearing surfaces or a dental implant bearing surfaces. An antimicrobial material such as silver may be deposited in combination with a metal to form an antimicrobial surface deposit.

Description

CROSS-REFERENCE TO RELATED DOCUMENTS[0001]This application is a divisional of:[0002]Pending U.S. patent application Ser. No. 11 / 624,041, filed Jan. 17, 2007 by Daniel F. Justin, et al. for LASER BASED METAL DEPOSITION (LBMD) OF ANTIMICROBIALS TO IMPLANT SURFACES, (Attorney's Docket No. MLI-58 NPROV), which is incorporated by reference, and is a non-provisional of:[0003]Prior U.S. Provisional Patent Application No. 60 / 811,934, filed Jun. 7, 2006 by Brent E. Stucker, et al. for INCORPORATION OF SILVER INTO MATERIALS DEPOSITED BY LBMD, (Attorney's Docket No. MLI-58 PROV), which is incorporated herein by reference.[0004]The following are also incorporated herein by reference:[0005]Issued U.S. patent application Ser. No. 11 / 432,426, filed May 10, 2006 by Daniel F. Justin et al. for LASER BASED METAL DEPOSITION (LBMD) OF IMPLANT STRUCTURES (Attorney's Docket No. MLI-05 CIP) issued as U.S. Pat. No. 7,666,522 on Feb. 23, 2010;[0006]Issued U.S. patent application Ser. No. 11 / 253,850 filed Oc...

AI Technical Summary

Benefits of technology

[0019]According to the LBMD material application of the present invention, the applied material can be applied as, for example, powdered metal, as a wire or as a foil. The applied material is then melted by a high-energy laser immediately upon or soon after application. The use of a laser to heat the applied material advantageously allows the heating to be very localized, thereby minimizing any adverse effects of such heat on the underlying material. However, in this invention, other sources of energy such as plasma and electron beam energy could also be focused and localized to allow energy based metal deposition of material through similar processes. Thus, in this invention laser energy is the preferred energy source. However it is understood that the term Laser Based Metal Deposition (LBMD) is meant to include any other energy source that can provide sufficient energy locally to melt and deposit the additive material, but minimize any adverse effects of such heat on the underlying base material.

[0037]The systems and methods of the present invention may be used to provide a number of different types of implant surfaces, including bone apposition surfaces, articular surfaces, and surfaces that do not abut bone or articulate. Bone apposition surfaces may be deposited with a relatively high porosity to enhance bone in-growth. Articular surfaces may be formed with a higher hardness to provide enhanced wear resistance. A wide variety of implant surfaces, including those that do not articulate or contact bone, may desirably be formed with antimicrobial properties to reduce the probability of infection of the tissues surrounding the implantation site.

Problems solved by technology

The development of such devices has confronted scientists and engineers with many technical challenges, such as in the area of materials science engineering wherein to achieve optimal implant performance various biocompatible materials with different physical and mechanical properties are bonded to each other.

Since a device such as an artificial joint must undergo a great number of cycles of wear during the lifetime of the host patient, such devices must also possess great fatigue properties.

While this produces an implant device with bulk properties that are optimized for certain overall design criteria such as biocompatibility strength and modulus of elasticity, these properties may not be optimized for property requirements specific to certain portions of the implant, such as wear or bone ingrowth characteristics.

For instance, while the use of porous materials such as porous Ti provides crucial and beneficial bonding properties, such materials may not have optimal properties in other areas.

For example, porous materials may not be as hard as some other biocompatible materials and therefore may not have acceptable wear properties.

However, because of the overriding importance of strong permanent bonding with the host patient bone, such porous materials have continued to be used in spite of less than optimal wear properties.

One challenge to using such a technique is that of achieving a sufficiently strong, permanent bond between the first and second portions, without the use of adhesives that may be biologically incompatible or may fail under the stresses imposed by the body of the patient.

Attempting to weld such materials together can cause the non-porous material to flow into the porous material, destroying the porosity of the porous material and degrading the ability of the device to bond with the patient's bone.

In addition, such materials, being dissimilar metals, often experience galvanic corrosion when bonded together in such a manner.