Soil solidifying agent

A soil curing agent and curing agent technology, applied in the direction of soil protection, soil conditioning materials, chemical instruments and methods, etc., can solve problems such as difficult compliance, poor early strength, large shrinkage, etc., to improve engineering performance and low cost , cost-effective effect

A soil curing agent and curing agent technology, applied in the direction of soil protection, soil conditioning materials, chemical instruments and methods, etc., can solve problems such as difficult compliance, poor early strength, large shrinkage, etc., to improve engineering performance and low cost , cost-effective effect

CN100371418CInactive Publication Date: 2008-02-27SOUTHEAST UNIV
4 Cites 7 Cited by

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Soil solidifying agent
  • Soil solidifying agent

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0017] The properties of the main raw materials used are as follows:

[0018] The soil is silt, and its performance indicators are shown in Table 1.

[0019] Table 1

[0020] density

(g / cm 3 )

optimal moisture content

dry density

(g / cm 3 )

plasticity index

(I P )

cosmid containing

quantity

Powder content

2.55

14.4％

1.79

6.8％

6.8％

88.3％

[0021] The cement is P.II.52.5 cement from Jingyang Cement Plant. The chemical composition and mineral composition of the clinker are shown in Table 2.

[0022] Table 2

[0023] chemical composition(%)

Mineral composition (%)

SiO 2

Al 2 o 3

Fe 2 o 3

CaO

MgO

SO 3

Burn out

quantity

C 3 S

C 2 S

C 3 A

C 4 AF

22.12

5.41 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
compressive strengthaaaaaaaaaa
strengthaaaaaaaaaa
Login to View More

Abstract

The soil curing agent as one kind of engineering material for curing and stabilizing various kinds of soil is especially suitable for curing silt and other kinds of low viscosity soil. The soil curing agent has main cement material comprising ore powder, flyash and water, as well as proper amount of alkali exciting component, expanding component and surfactant, and is prepared through mixing the materials and grinding to Blaine fineness of 3000-5000 sq m / kg. Specifically, it consists of mineral admixture 40-60 wt%, cement 15-25 wt%, alkali exciting component 5-15 wt%, expanding component 15-25 wt% and surfactant 0.01-0.1 wt%.

Description

technical field [0001] The invention relates to an engineering material capable of solidifying and stabilizing various types of soil, and is especially suitable for curing treatment of low-cohesive soil foundations such as silt, and belongs to the technical field of civil construction material manufacturing. Background technique [0002] At present, the research on soil stabilization and solidification technology in my country is still in a relatively backward state. The soil stabilization and stabilization materials are still dominated by cement, lime, fly ash or simple mixtures of these materials. Many problems have been solved, and it is difficult to meet the requirements of actual engineering, mainly reflected in poor early strength, large shrinkage, easy cracking, poor stability (water stability, freezing stability, thermal stability), etc., especially silty , Sandy areas, these problems will be more prominent. Contents of the invention [0003] Technical problem: the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
27 Feb 2008
Publication
CN100371418C
IPC
C09K17/00; E02D3/12
Inventors
钱春香; 刘松玉