Compound molten iron desulfurizer
A molten iron desulfurization and composite technology, applied in the field of composite molten iron desulfurizers, can solve the problems of reducing desulfurization effect and the like
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment Construction
[0007] The weight percentage of each component of the composite hot metal desulfurizer of the present invention is: active lime 60-75, calcium aluminate 5-8, passivation magnesium 4-10, metal aluminum 5-10, calcium fluoride 4-7, and the rest are Impurities. In specific use, it should be flexibly adjusted according to the quality of the raw materials of the desulfurizer and the sulfur content of the molten iron to be treated.
[0008] As a specific embodiment of the present invention, the formula is: activated lime 70, calcium aluminate 6, passivated magnesium 8, metal aluminum 8, calcium fluoride 6, the rest are impurities, and the sum of the above components is 100%. In order to further reduce the cost, you can replace the aluminum powder with the chips generated during the machining of aluminum products, heat the aluminum chips at high temperature to remove the oil, and then crush them for use.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com