Dreg ball free alumina silicate cotton velvet and its uses in brake field

A technology of aluminum silicate and slag balls, which is applied in the manufacture of tools and glass manufacturing equipment, etc., to achieve the effects of prolonged service life, stable friction coefficient and low noise

Active Publication Date: 2009-06-24
LUYANG ENERGY SAVING MATERIALS CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, the conventional production of aluminum silicate fiber, no matter it adopts melt-spinning or melt-blown fiber formation, uses external force to elongate the high-temperature molten droplet, and there are different degrees of slag balls in the product fiber, usually φ≥0.25mm Slag content generally ≥ 20%

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Example 1 Preparation of brake pads for mining machinery

[0037] Use ordinary slag-free aluminum silicate cotton wool, its physical properties are

[0038] Fiber length 250~300μm±30

[0039] Fiber diameter 2~5μm

[0040] Does not contain slag balls of φ≥0.25mm

[0041] Mohs hardness 5~7

[0042] Operating temperature 1000~1300℃

[0043] Thermal conductivity W / mk 0.153

[0044] (500±20℃)

[0045] Tensile strength 1000~1600MPa

[0046] Does not contain slag balls with φ≤0.25mm.

[0047] The chemical composition is Al 2 o 3 43%, SiO 2 57%.

[0048] Use a special opener or fiber cutter to open, clean, crush, and screen ceramic fibers to separate cotton and slag, shorten fiber length, and reduce slag ball content to obtain aluminum silicate cotton wool , φ≥0.25mm slag ball content≤0~8%.

[0049] Manufactured according to the conventional brake pad method, the adhesive is made of phenolic resin or modified phenolic resin plus rubber, the amount of adhesiv...

Embodiment 2

[0053] Example 2 Preparation of brake pads for petroleum machinery

[0054] Use ordinary slag-free aluminum silicate cotton wool

[0055] Its physical properties are

[0056] Fiber length 50~150μm±30

[0057] Fiber diameter 2~5μm

[0058] φ≥0.25mm slag ball content 6~8%

[0059] Mohs hardness 5~7

[0060] Operating temperature 1000~1300℃

[0061] Thermal conductivity W / mk 0.150

[0062] (500±20℃)

[0063] Tensile strength 1000~1600MPa

[0064] Its chemical composition is Al 2 o 3 55%; SiO 2 45%; All the other are with embodiment 1.

Embodiment 3

[0065]Example 3 Preparation of brake pads for automobiles

[0066] To make zirconium-containing slag-free aluminum silicate cotton wool, its physical properties are

[0067] Fiber length 200~300μm±30

[0068] Fiber diameter 2~5μm

[0069] Mohs hardness 5~7

[0070] Operating temperature 1000~1300℃

[0071] Thermal conductivity W / mk 0.140

[0072] (500±20℃)

[0073] Tensile strength 1000~1600MPa

[0074] Does not contain slag balls with φ≥0.25mm.

[0075] The chemical composition is Al 2 o 3 +SiO2 2 +ZrO 2 99.5%, of which, ZrO 2 ≥15%; impurity balance, all the other are the same as embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
tensile strengthaaaaaaaaaa
Mohs hardnessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a slag-free aluminum silicate cotton wool and its application in the braking field. Contains ordinary type, zirconium-containing type and soluble aluminum silicate fiber lint, the fiber length is 50-300μm±30, the diameter is 2-5μm, the slag content of φ≥0.25mm is 0-8%, and the Mohs hardness is 5-7 , use temperature 1000~1300℃, thermal conductivity W / mk, 500±20℃≤0.153, tensile strength 1000~1600Mpa; chemical composition is Al2O343~55%, SiO245~57%; or Al2O3+SiO2+ZrO298.5~ 99.5%, of which, ZrO2≥15%, impurity balance; or SiO2 52~85%, CaO 5~35%, MgO 1~10%, Al2O30~1%, B2O31~2%; used as fiber reinforcement in the braking field material application.

Description

technical field [0001] The invention belongs to the category of mechanical motion braking, and in particular relates to a slag-free aluminum silicate cotton wool and its application in the braking field. Background technique [0002] Braking material (also known as friction material), as a composite material with a high friction coefficient, is a key part of various machine brakes. It affects the reliability of the machine and the safety of driving and personal. , transportation machinery, chemical machinery, mining machinery, petroleum machinery and other machinery are indispensable. [0003] Brake materials are safety-critical components in clutch assemblies and brakes for vehicles and machinery. It is generally composed of three parts: binder, fiber reinforced material and filler. [0004] In the past, fiber reinforced materials were mainly asbestos products, but asbestos products have been eliminated due to environmental protection reasons. Due to its good heat resist...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C03B37/00C03B37/005C04B14/04
Inventor 鹿成洪鹿俊华张明全崔春海任大贵李京友
Owner LUYANG ENERGY SAVING MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap