Method of raising compatibility between ABS and polymethyl methacrylate

A polymethyl methacrylate, compatibility technology, applied in the field of thermoplastic resin compositions, can solve problems such as uneven distribution, uneven surface hardness of alloy products, etc., to achieve improved compatibility, uniform hardness distribution, excellent tensile strength The effect of tensile and bending properties

Inactive Publication Date: 2009-07-08
MITAC PRECISION TECH CO LTD SHUNDE DISTRICT FOSHAN CITY
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the blending modification of ABS and PMMA, since ABS and PMMA are partially compatible systems, direct use of ABS and PMMA for modification and granulation is likely to cause uneven distribution of the two in the alloy, resulting in uneven surface hardness of alloy products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method of raising compatibility between ABS and polymethyl methacrylate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Weigh ABS and PMMA raw materials according to the weight ratio of 100:25, add 3.8 parts of MBS after mixing, then mix evenly in a high-speed mixer, transfer to a twin-screw extruder to melt and blend at 180-220°C, pressure 60- 80Mpa, the material stays for 2 minutes; the material is discharged, cooled, dried and pelletized after extrusion to obtain the finished product.

Embodiment 2

[0018] Weigh ABS and PMMA raw materials according to the weight ratio of 100:30, add 5 parts of MBS after mixing, then mix evenly in a high-speed mixer, transfer to a twin-screw extruder to melt and blend at 180-220°C, pressure 60- 80Mpa, the material stays for 2 minutes; the material is discharged, cooled, dried and pelletized after extrusion to obtain the finished product.

Embodiment 3

[0020] Weigh ABS and PMMA raw materials according to the weight ratio of 100:27, add 4 parts of MBS after mixing, then mix evenly in a high-speed mixer, transfer to a twin-screw extruder to melt and blend at 180-220°C, pressure 60- 80Mpa, the material stays for 2 minutes; the material is discharged, cooled, dried and pelletized after extrusion to obtain the finished product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for improving the compatibility of ABS and polymethyl methacrylate. The method is to fully mix 100 parts of ABS, 25-30 parts of PMMA and 3.8-5 parts of MBS calculated by weight ratio, and then use Melt blending extrusion one-step preparation. The method provided by the invention has simple process and low cost. MBS is added to the ABS / PMMA alloy system as a modifier, so that the two-phase system is evenly distributed after ABS and PMMA are granulated, and the compatibility between them is improved. , the surface hardness distribution of the obtained ABS / PMMA alloy is uniform, and at the same time endows ABS with more excellent tensile and bending properties, expanding the industrial application range of ABS.

Description

technical field [0001] The invention relates to the field of thermoplastic resin compositions in polymer material technology, in particular to a method for improving the compatibility of ABS and polymethyl methacrylate. Background technique [0002] ABS (Acrylonitrile Butadiene Styrene, acrylonitrile-butadiene-styrene copolymer) refers to a terpolymer composed of acrylonitrile, butadiene and styrene. Because ABS has good molding processability, the surface finish of the product is high , and has good paintability and dyeability, can be electroplated into various colors, combined with excellent performance, reasonable price and easy processing and molding, it has become the thermoplastic engineering plastic with the highest output and widest application. It is widely used in the automotive industry, Electrical and electronic industry, light industrial appliances, textiles, construction and other industries. [0003] Due to the low surface hardness of ordinary ABS products co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L55/02B29B7/18B29B9/12C08L33/12
Inventor 周静冯小伟
Owner MITAC PRECISION TECH CO LTD SHUNDE DISTRICT FOSHAN CITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products