Plate blank electroslag furnace

An electroslag furnace and slab technology, applied in the field of slab electroslag furnace, can solve the problems of incomplete controlled rolling equipment, low rolling pressure, steel plate flaw detection, etc. The effect of melting speed

Active Publication Date: 2007-07-25
NORTHEASTERN UNIV LIAONING
View PDF0 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The existing electroslag furnace cannot meet the above-mentioned steel requirements, and the steel ingots produced by the existing equipment have low purity and small compression ratio, which is prone to inconsistencies in flaw detection defects inside the steel plate; low rolling pressure, temperature control, and The rolling equipment is not complete, the heat treatment equipment is not perfect, resulting in insufficient strength level of the steel plate; the single weight of the specification cannot meet

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Plate blank electroslag furnace
  • Plate blank electroslag furnace
  • Plate blank electroslag furnace

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] Embodiment 1: The crystallizer in the present invention adopts a T-shaped crystallizer, the power supply is AC, and the power supply mode of bipolar series. As shown in Figure 1 and Figure 2, it includes an AC power supply 15, an electrode lifting mechanism 1, a rotating frame 2, a load cell 3, an electrode I4, an electrode II5, a T-shaped crystallizer 6, a supporting platform 8, and an ingot pulling mechanism 13, Dummy device 11, ingot transport trolley 12, molten steel liquid level detection device 10 and control system 14, crystallizer 6 is fixed on the support platform 8, on the support platform 8 is fixed a rotating frame 2, the rotating frame 2 can move along the support platform The fixed track on 8 rotates, and an adjustment mechanism is installed on the rotating frame 2, which is used for adjusting the electrode lifting mechanism in the horizontal X and Y directions. The electrode lifting mechanism 1 is placed on the frame platform 18 in the rotating frame 2, an...

Embodiment 2

[0063] Example 2: The crystallizer in the present invention adopts a unipolar, T-shaped conductive crystallizer. The T-shaped conductive crystallizer used is a conductive ring placed between the upper part of the crystallizer and the lower part of the crystallizer, and the upper part of the crystallizer and the conductive ring are Insulators are respectively arranged between the lower part of the crystallizer and the conductive ring; the insulator is made of ceramic material, and the conductive ring is made of copper. The power supply is AC, and the power supply mode is single-electrode, T-shaped mold conductive. As shown in Figures 3 and 4, it includes an AC power supply 15, an electrode lifting mechanism 1, a rotating frame 2, a load cell 3, an electrode 14, a mold 6, a supporting platform 8, an ingot pulling mechanism 13, a dummy device 11 and The control system 14, the crystallizer 6 is fixed on the supporting platform 8, the rotating frame 2 is fixed on the supporting pla...

Embodiment 3

[0066] Example 3: The crystallizer in the present invention adopts a barrel type crystallizer, the power supply is DC, and the bipolar power supply mode is connected in series. As shown in Figures 5 and 6, it includes an AC power supply 15, an electrode lifting mechanism 1, a rotating frame 2, a load cell 3, an electrode I4, an electrode II5, a T-shaped mold 6, a support platform 8, an ingot pulling mechanism 13, The dummy device 11, the ingot transporting trolley 12, the molten steel level detection device 10 and the control system 14, the mold 6 is fixed on the support platform 8, the rotating frame 2 is fixed on the support platform 8, and the rotating frame 2 is mounted on the rotating frame 2. Adjustment mechanism, the electrode lifting mechanism 1 is placed on the frame platform 18 in the rotating frame 2, and a load cell 3 is placed between the contact surface of the electrode lifting mechanism 1 and the frame platform 18, the model is 1-RTNAED9301A, electrode I4 and ele...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

This invention discloses a slab electroslag furnace, which comprises: an AC power supply, an electrode elevator, an electrode, a crystallizer, a support platform, an ingot feeder, a liquid level detector of molten steel, a rotary frame, a weight sensor, an ingot discharger, and a control system. The crystallizer is fixed in the support platform. The rotary frame is fixed on the support platform, and can move along a fixed track. The electrode elevator is set on the platform of the rotary frame, and can be horizontally adjusted. The weight sensor is set at the contact surface of the electrode elevator and the platform of the rotary frame. One end of the electrode (monopolar or bipolar) is fixed with the electrode elevator, and the other one is set in the crystallizer. The liquid level detector of molten steel is set on the sidewall of the crystallizer. The ingot discharger is set on a frame below the support platform. A wagon is fixed on the ingot discharger. The ingot feeder is fixed in the wagon. The control system, elevator, weight sensor, ingot discharger and wagon are electrically connected.

Description

technical field [0001] The invention belongs to the technical field of metal electroslag remelting equipment, and particularly relates to a slab electroslag furnace, which is applied in the process of metal remelting and smelting. Background technique [0002] Electroslag furnace is a kind of metallurgical equipment that uses the resistance heat generated when electric current passes through molten slag as a heat source to smelt metal. After electroslag remelting, the content of gas and inclusions in the steel can be reduced, and a steel ingot with uniform composition, dense structure and excellent quality can be obtained. The ductility and toughness of the alloy, especially the transverse properties, are improved, anisotropy is reduced, and various macroscopic and microscopic defects are eliminated or mitigated. Therefore, electroslag furnace equipment has been widely used in steel, machinery and other industries at home and abroad. [0003] At present, domestic electrosl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22B9/187
Inventor 姜周华余强臧喜民张天彪任安生
Owner NORTHEASTERN UNIV LIAONING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap