Composite board made of natural firilia for automobile inner decoration use and its producing method

A fiber composite board and processing method technology, which is applied in wood processing appliances, applications, household components, etc., can solve the problems of less use of natural fibers, complex production processes, low board strength, etc., so as to improve production efficiency and reduce processing procedures. , the effect of increasing strength

Active Publication Date: 2007-10-03
铜陵华源汽车内饰材料有限公司
View PDF1 Cites 44 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage is that the production process is complicated and the production efficie

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite board made of natural firilia for automobile inner decoration use and its producing method
  • Composite board made of natural firilia for automobile inner decoration use and its producing method
  • Composite board made of natural firilia for automobile inner decoration use and its producing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Embodiment 1: to produce 1600g / m 2 Taking natural hemp composite fiberboard as an example, the specific gravity of each layer is 200g / m2 for the rubber surface layer 2 , middle base layer 1220g / m 2 , fabric layer 180g / m 2 . The proportion of fibers used in each layer is:

[0018] Rubber surface layer: 50% polypropylene fiber, 50% polyethylene fiber.

[0019] Middle base layer: 37% jute fiber, 10% polyester fiber, 53% polypropylene fiber.

[0020] Fabric layer: 30% polypropylene fiber, 70% polyester fiber.

[0021] The polyester fiber used in the fabric layer is black polyester fiber, with a specification of 1.5 to 2 denier (denier: the weight of a fiber with a length of 9 km at a given moisture regain), and the polyester fiber used in other layers is white polyester fiber, with a specification of 1.5 to 2 denier , The length of polyester fiber is 51-65 mm; the specification of polypropylene fiber is 5-6 denier, and the fiber length is 74-78 mm; hemp fiber is cut i...

Embodiment 2

[0027] Embodiment 2: the ratio of each layer of fiber is:

[0028] Rubber surface layer: 70% polypropylene fiber, 30% polyethylene fiber.

[0029] Intermediate base: 45% jute fiber, 20% polyester fiber, 35% polypropylene fiber.

[0030] Fabric layer: 50% polypropylene fiber, 50% polyester fiber.

[0031] Processing method is with embodiment 1. The performance of the obtained board: the thickness of the board is 3.5 mm, the bending strength is 9.97 MPa, the tensile strength is 9.33 MPa, and the elongation at break is 12.31%.

Embodiment 3

[0032] Embodiment 3: the ratio of each layer of fiber is:

[0033] Rubber surface layer: 90% polypropylene fiber, 10% polyethylene fiber.

[0034] Middle base layer: jute fiber 41%, polyester fiber 14%, polypropylene fiber 45%.

[0035] Fabric layer: 40% polypropylene fiber, 60% polyester fiber.

[0036] Processing method is with embodiment 1. The performance of the obtained board: the thickness of the board is 3.5 mm, the bending strength is 7.83 MPa, the tensile strength is 7.66 MPa, and the elongation at break is 13.53%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Bending strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

A composite bast fiber board for the internal decoration of car is composed of adhesive layer, sandwich substrate layer and surface layer, and is prepared through sequentially spreading said three layers, needling to become a composite bast felt, and hot pressing. Said sandwich substrate is made of the mixture of bast fibers (37-45%), polyester fibers (10-20%) and polypropylene fibers (35-53%).

Description

Technical field [0001] The invention relates to a composite board made of natural plant fibers and chemical fibers and mainly used for automotive interior parts. Background technique [0002] With the improvement of people's requirements for environmental protection, the materials of automotive interior parts are developing in the direction of "green" environmental protection materials. Some materials used in the production of automotive interior parts in the early stage, such as PU board (polyurethane board), glass steel and other materials, due to The deficiencies in pollution are gradually being replaced by natural hemp fiber composite materials. The processing of natural hemp fiber composites usually involves mixing natural fibers and chemical fibers into felt boards and then heating and pressing them. Such as the patent document of CN1605462A discloses such a kind of environment-friendly thermoplastic natural brown hemp fiber automotive interior trim composite substrat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B27N3/04B27N3/08
Inventor 左春生刘亚平潘忠共梅皓然
Owner 铜陵华源汽车内饰材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap