Milling of energy-saving type glassed steel overglaze added with ultra-fine zro* powder body as fortifier

A reinforcing agent and energy-saving technology, applied in the field of glass-lined glaze, can solve the problems of rapid temperature change resistance, failure to meet performance requirements, limitations, etc.

Inactive Publication Date: 2008-02-27
JIANGYIN SILICON GENERAL ENAMEL
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] Conventional glass-lined surface glazes are limited by production process conditions due to wear resistance, impact strength, thermal stress resistance, and rapid temperature difference resistance.
It cannot meet the occasions with high performance requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] (1), frit composition (weight part):

[0024] SiO 2 42

[0025] B 2 o 3 3

[0026] al 2 o 3 1

[0027] TiO 2 9

[0028] ZrO 2 3

[0029] K 2 O+NaO 2 10

[0030] Li 2 O 5

[0031] CaO+MgO 1.5

[0032] BaO 14.5

[0033] CoO 1.00

[0034] 2. Grinding ratio: frit 100, 400-500 mesh zircon powder 45, suspending agent clay 3.5. The physical and chemical properties of the glass lining are:

[0035] Burning temperature

Embodiment 2

[0037] (1), frit composition (weight part):

[0038] SiO 2 43.5

[0039] B 2 o 3 6.5

[0040] al 2 o 3 1.6

[0041] TiO 2 5.2

[0042] ZrO 2 0.5

[0043] K 2 O+NaO 2 8.0

[0044] Li 2 O 3.5

[0045] CaO+MgO+BaO 15.0

[0046] CoO 1.0

[0047] (2) grinding ratio (parts by weight):

[0048] Frit 100, zircon powder (400-500 mesh) 45, suspending agent clay 3.5.

[0049] The physical and chemical properties of the glass lining are:

[0050] Burning temperature

(℃)

heat resistant sodium hydroxide

(g / m 2 d)

Resistant to boiling hydrochloric acid

(g / m 2 d)

Resistance to sudden changes in temperature difference

(℃)

wear resistance

(mg / cm 2 / h)

860

2.2

0.45

360

2.5

[0051] The present invention also provides the preparation method of the glass-lined glaze that uses above-mentioned formula, and it mainly compri...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an energy-saving glass lining cover coat based on mill addition hyperfin ZrO2 powder as reinforcer, which consists of clinker clew and mill addition material, wherein the clinker clew includes 45-5% SiO2+B2O3, 7-12% Na2O+K2O, 12-16% MgO+CaO+BaO, 3. 5-6% Li2O, 1-2% CoO,6-15% ZrO2+Al2O3+TiO2; the mill addition material contains 40-60% zircon powder at 400-500 order and 3-5% suspending agent clay. The glass phase is main component of regular glass lining cover coat, which changes the structure of ceramic glaze after adding the hyperfine ZrO2 powder to harden the glass lining with more abrasion proof. The invention leads Li2O to reduce the softening point of cover coat clinker clew because the hyperfine ZrO2 powder mill addition is added into the glass lining cover coat to increase the sintering temperature, which makes the sintering temperature of cover coat nearly approach the temperature of regular glass lining cover coat.

Description

technical field [0001] The invention relates to a glass-lined glaze, in particular to a grinding and adding ultrafine ZrO 2 Energy-saving glass-lined glaze with powder as reinforcing agent. Background technique [0002] The so-called glass-lined glaze is an enamel glaze that is resistant to strong acid corrosion. Because its formula and melting process are close to glass, it is called glass-lined glaze. Conventional glass-lined glaze is close to sodium-aluminum-titanium-zirconium-boron-silicate glass, and a small amount of colorant is added. [0003] The formula of conventional glass-lined surface glaze is composed as follows (percentage by weight): [0004] 1. Frit [0005] Matrix agent: SiO 2 +B 2 o 3 =70~76 [0006] Flux: Na 2 O+K 2 O=14~18 MgO+CaO=3~5 [0007] Colorant: CoO+MnO=1~2 [0008] Refractory composition: ZrO 2 +Al 2 o 3 +TiO 2 =5~10 [0009] 2. Grinding material: its composition is based on the weight of the glaze block as 100 [0010] Suspend...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/20
Inventor 余献忠
Owner JIANGYIN SILICON GENERAL ENAMEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More