Composition of surface chemistry plating liquid and preparation method for wooden electromagnetic screen material

A technology of surface chemistry and composition, which is applied in the field of composition of chemical plating solution on the surface of wood materials, can solve the problems such as failure to effectively solve the defects of wood materials itself, and achieve health and safety protection, added value, and surface decoration Effect

Inactive Publication Date: 2011-04-27
BEIJING FORESTRY UNIVERSITY
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Through these two approaches, the limitations of wood in use performance can be overcome to a certain extent, and the performance of wood can be improved, but the inherent defects of wood materials have not been effectively solved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] (a) Poaching treatment:

[0055] The air-dried poplar wood was sliced ​​into veneers with a thickness of 0.6 mm, boiled in hot water at 60°C for 10 minutes to remove the extracts from the poplar veneers, and then dried to absolute dryness.

[0056] (b) Surface treatment:

[0057] Put the poplar veneer processed through step (a) into a surface treatment solution consisting of 1.0 parts by weight of 3-aminopropyltrimethoxysilane and 9.0 parts by weight of ethanol solution for 5 min, then take out the poplar veneer Dry in the air, after the solvent on the surface of the poplar veneer volatilizes, put it in a drying oven, and dry it at 105°C for 2 hours.

[0058] (c) Surface sensitization and activation treatment:

[0059] Put the poplar veneer after the surface treatment in step (b) into a sensitizer solution composed of 3.0 parts by weight of tin chloride and 7.0 parts by weight of hydrochloric acid solution for 20 seconds, then wash it with water and then dip it in 5.0...

Embodiment 2

[0066] (a) Poaching treatment:

[0067] The air-dried Chinese fir was sliced ​​into shavings with a thickness of 0.5mm, boiled in hot water at 60°C for 15 minutes to remove the extractives in the wood, and then dried to absolute dryness.

[0068] (b) Surface treatment:

[0069] The shavings obtained by step (a) are put into a surface treatment solution composed of 1.0 parts by weight of 3-aminopropyltrimethoxysilane and 9.0 parts by weight of ethanol solution and immersed for 8 minutes, then take out the shavings and dry them in the air. After the solvent on the surface of the shavings evaporated, put them in a drying oven and dry them at 103°C for 1 hour.

[0070] (c) Surface sensitization and activation treatment:

[0071] Put the shavings after the surface treatment in step (b) into a sensitizer solution composed of 3.0 parts by weight of tin chloride and 7.0 parts by weight of hydrochloric acid solution for 40 seconds, then wash them with water and then immerse them in a...

Embodiment 3

[0080] (a) Poaching treatment:

[0081] Air-dried poplar wood was sliced ​​into veneers with a thickness of 0.7mm, boiled in hot water at 70°C for 5 minutes to remove extracts from the poplar veneers, and then dried to absolute dryness.

[0082] (b) Surface treatment:

[0083] Put the poplar veneer processed through step (a) into a surface treatment liquid composed of 1.0 parts by weight of trimethoxysilane and 9.0 parts by weight of ethanol solution for 10 minutes, then take out the poplar veneer and cool it in the air After the solvent on the surface of the poplar veneer volatilizes, put it in a drying oven and dry it at 107°C for 2.5 hours.

[0084] (c) Surface sensitization and activation treatment:

[0085] Put the poplar veneer after the surface treatment in step (b) into a sensitizer solution composed of 3.0 parts by weight of tin chloride and 5.0 parts by weight of hydrochloric acid solution for 30 seconds, then wash it with water and dip it in 5.0% chloride Platinu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention provides one kind of chemical plating liquid composition for wooden material and the process of preparing electromagnetic shielding material on the surface of wooden material. The chemical plating liquid composition consists of metal salt 2.0-7.0 weight portions and complexing agent 3.0-6.0 weight portions. The chemical plating process includes the steps of water boiling of wooden material, surface treating, surface sensitizing and activating, reducing and surface chemical plating. The obtained electromagnetic shielding material has an electromagnetic shielding effectiveness in the frequency range of 5 KHz-1500 MHz up to 31.8dB-51.4dB. The present invention can raise the surface decoration effect of wooden material, endows wooden material with conducting performance and electronic shielding performance, raise the application value and use safety of wooden material.

Description

technical field [0001] The invention relates to a composition for surface chemical plating solution, in particular to a composition for surface chemical plating solution of wooden materials and a method for preparing wooden electromagnetic shielding material using the composition. Background technique [0002] Wood is widely used in every link of national economic development, from people's daily living utensils, furniture, interior decoration and furnishing components to packaging supplies, transportation tools, sports equipment to large buildings, wood plays an important role. The use of wood has witnessed the development of human civilization. [0003] As the most typical biocomposite material, wood has the advantages of large strength-to-weight ratio, good heat insulation, sound insulation, low processing energy consumption, less environmental pollution, renewable, and natural degradation. However, wood also has some disadvantages, such as properties Large variability, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C18/16C23C18/34C23C18/20C23C18/28
Inventor 赵广杰黄金田马晓军商俊博
Owner BEIJING FORESTRY UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com