Polyethylene terephthalate composite material and method of producing the same

A technology of polyethylene terephthalate and composite materials, which is applied in the direction of liquid crystal materials, chemical instruments and methods, etc., can solve problems such as narrow application areas, unsatisfactory requirements, and few varieties of industrial production, so as to meet the needs, Wide range of applications and the effect of increasing the crystallization rate

Active Publication Date: 2008-04-02
HEFEI GENIUS NEW MATERIALS
View PDF0 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Inorganic salt is a low-cost crystallization nucleating agent, but affected by the particle size and degree of dispersion, it is very limited in improving the crystallization rate of polyethylene terephthalate, which is far from meeting the requi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyethylene terephthalate composite material and method of producing the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] 70 parts of polyethylene terephthalate, carapace liquid crystal poly[vinyl terephthalate (p-methoxyphenol) ester] (PMPCS) molecular weight 15000, 1 part of molecular weight distribution 1.5, crystallization accelerator polyethylene glycol 5 parts of alcohol and 1 part of other additives are mixed by high-speed stirring. Then it is sent into the twin-screw extruder by the precision metering feeder, and then 23 parts of the glass fiber filled with reinforcing agent are sent into the twin-screw extruder from the precision metering feeder, plasticized, melted, compounded, and then extruded, Stranding, cooling, pelletizing, drying and packaging the finished product.

Embodiment 2

[0018] 80 parts of polyethylene terephthalate, carapace liquid crystal poly[vinyl terephthalate (p-methoxyphenol) ester] (PMPCS) molecular weight 25000, 1 part of molecular weight distribution 1.3, crystallization accelerator polypropylene glycol 4 1 part and 1 part of other additives are stirred and mixed at high speed, and then sent into the twin-screw extruder by a precision metering feeder, and then 13 parts of glass fiber filling reinforcement are sent into the twin-screw extruder from the precision metering feeder, Plasticizing, melting, compounding, and then extruding, drawing, cooling, pelletizing, drying and packaging the finished product.

Embodiment 3

[0020] 60 parts of polyethylene terephthalate, carapace liquid crystal poly[vinyl terephthalate (p-methoxyphenol) ester] (PMPCS) molecular weight 35000, 1 part of molecular weight distribution 1.8, 6 parts of crystallization accelerator and 1.7 parts of other additives are mixed with high-speed stirring, and then sent to the twin-screw extruder by a precision metering feeder, and then 31 parts of carbon fiber filled with a reinforcing agent are sent to the twin-screw extruder from the precision metering feeder, plasticized , melting, compounding, and then extruded, drawn, cooled, pelletized, dried and packaged.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention relates to a polyethylene terephthalate composite material and the preparation method. The method comprises: 40 weight portion to 80 weight portion of polyethylene terephthalate, 0.1 weight portion to 4 weight portion of macromolecule nucleating agent testa liquid crystal, 1 weight portion to 6 weight portion of macromolecule crystallization accelerator, and 0.5 weight portion to 1 weight portion of other processing aids are stirred and mixed at a high speed; the mixture is then sent into a double-screw extruder through a material feeder of precise measurement. Then 10 weight portion to 50 weight portion of intensifier is filled into the double-screw extruder through the material feeder of precise measurement. The product can be prepared after plasticization, melting, compounding, and then extruding, bracing, cooling, pelletizing and drying. Compared with the prior art, the present invention has the characteristics of improving the crystallization rate of polyethylene terephthalate, widening the application scope, meeting the demands of engineering plastics for polyethylene terephthalate.

Description

technical field [0001] The invention relates to the field of polymer material engineering plastics and its molding processing, in particular to a PET composite material containing carapace liquid crystal as a nucleating agent and a preparation method thereof. Background technique [0002] Polyethylene terephthalate (PET) is a crystalline high polymer with excellent comprehensive properties. However, due to the high rigidity of the main chain of PET and the slow movement of chain breaking, the crystallization speed is slow. The application in the field of engineering plastics is limited, specifically: high injection mold temperature, long molding cycle, easy mold sticking and warping of products, thus greatly limiting its application in the field of engineering plastics. [0003] Improving the crystallization rate is the key to improving the molding processability of polyethylene terephthalate (PET). At present, research in this area is still in the stage of laboratory explo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L67/03C09K19/38B29C47/40B29B9/12
Inventor 王鹏解廷秀杨桂生
Owner HEFEI GENIUS NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap