Compound energy-saving antiwear agent of organic boron and method of producing the same

A technology of organic boron and anti-wear agent, which is applied in the field of anti-wear agent, can solve the problems such as not being able to lubricate parts exposed to water, achieve good maintenance effect, simple and easy-to-operate preparation method, and scientific compatibility

Inactive Publication Date: 2008-04-02
吴桂琴
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, since borate is soluble in water, and it requires a certain amount of crystal water to have the best extreme pressure performance, it cannot be used for lubrication of water-seeping parts.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Compound energy-saving antiwear agent of organic boron and method of producing the same
  • Compound energy-saving antiwear agent of organic boron and method of producing the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 5

[0030] Embodiment 5, embodiment 6, embodiment 7, embodiment 8 are the embodiments of organoboron performance measurement.

Embodiment 9

[0031] Example 9 is an example of performance measurement of organic boron composite energy-saving and anti-wear agent.

Embodiment 1

[0033] (1) Sulphurphosphating reaction: In a four-necked reaction flask equipped with a stirrer, a thermometer, an air duct and a gas absorption device, first add 176g (2mol) of sec-amyl alcohol and 260g (2mol) of 2-ethylhexanol , stir and pass N 2 Under protective conditions, 222 g (1 mol) of phosphorus pentasulfide was added dropwise in batches, the rate of addition was controlled to avoid too fast a temperature rise, the temperature was controlled at 90±2°C, and the reaction was performed at a constant temperature for 3-5 hours. The H produced by the reaction 2 S gas imports the absorption bottle that 178g30% concentration NaOH solution (1.33mol) is housed, converts into Na after the completion of the reaction 2 212g of S and NaHS mixed solution was used for later use. The reactant in the four-neck flask is filtered after cooling, and obtains the micro-black transparent liquid of second amyl isooctyl dithiophosphoric acid, weighs 612g, yield 98.1%, acid value 146mgKOH / g, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
boiling pointaaaaaaaaaa
acid valueaaaaaaaaaa
acid valueaaaaaaaaaa
Login to View More

Abstract

The invention relates to the anti-abrasion agent field, in particular to an organic boron complex energy saving anti-abrasion agent and a preparation process thereof. The compositions by weight percentage of the organic boron complex energy saving anti-abrasion agent are as follows: organic boron: 40 to 80 percent; petroleum sulfonate of barium: 5 to 15 percent; isobutylene boride: 10 to 30 percent; sulfurized isobutylene: 5 to 15 percent. The organic boron complex energy saving anti-abrasion agent has scientific formula, reasonable design and good anti-abrasion, water-resistant and anti-rust performance, can form a boronization laminated film with elasticity and strong adhesive force by being absorbed on the friction surfaces to play a role of apparent abrasion reduction and abrasion resistance, can be widely used in the lubricating systems of various machines, equipment and vehicles, and has good maintenance effect and certain energy saving effect.

Description

technical field [0001] The invention relates to the field of antiwear agents, in particular to an organic boron composite energy-saving antiwear agent and a preparation method thereof. Background technique [0002] The anti-wear agent can greatly reduce the frictional resistance of the protected machinery, save power energy, and prolong the life of the machinery exponentially. With the development of sulfur-phosphorus gear oils and hydraulic oils, boron-containing additives have begun to be used in such oils. Borates are a new type of environment-friendly extreme pressure anti-wear agent. Studies have shown that its extreme pressure performance, anti-wear performance, thermal oxidation stability, high temperature corrosion resistance and airtight performance are superior to some other types of extreme pressure agents. For example, the heat resistance temperature of general sulfur and phosphorus agents is about 130 ° C , while the heat-resistant temperature of borate is 150°...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M139/00C10M135/10C10N30/06
Inventor 吴桂琴
Owner 吴桂琴