Urethane micro-pore elastomer composite material adapated for insole and preparation method thereof

A microporous elastomer, polyurethane technology, applied in insoles, applications, footwear, etc., can solve problems such as low strength, and achieve the effects of low production cost, stable product quality, and simple process

Active Publication Date: 2008-04-23
SHANDONG INOV POLYURETHANE
View PDF0 Cites 33 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to provide a combination of polyurethane microporous elastomers suitable for insoles and its p

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Prepare 100 kilograms of component A materials, weigh respectively: polyether polyol (3 functionalities, molecular weight is 5000, primary hydroxyl content 70%, unsaturation 0.005mmol / L) 50 kilograms, polymer polyol (styrene-linked Branch copolymerization, solid content 30%, POP93 / 28, Shandong Dongda Chemical Co., Ltd. product) 45 kilograms, linking agent (with triethanolamine as initiator, molecular weight is the polyoxypropylene polyol of 200) 2.5 kilograms, Catalyst triethylenediamine 0.5 kg, water 1.5 kg, B8905 0.5 kg. Put the weighed polyether polyol and polymer polyol materials into the reaction kettle and stir, then add the weighed crosslinking agent, catalyst, foaming agent, stabilizer, and stir the combined reaction at normal temperature, stirring for 3.5 hour, take it out for inspection, meet the process parameters, and emit satisfactory foam, that is, the qualified product of component A is obtained, and it is taken out from the reactor and put into a barrel ...

Embodiment 2

[0040] Prepare 100 kilograms of component A materials, weigh respectively: polyether polyol (3 functionalities, molecular weight is 6000, primary hydroxyl content 70%, unsaturation 0.005mmol / L) 45 kilograms, polymer polyol (styrene-linked Branch copolymerization, solid content 30%, with embodiment 1 product) 50 kilograms, crosslinking agent (take triethanolamine as initiator, molecular weight is 3 kilograms of polyether polyols of 200, 0.5 kilograms of catalyzer triethylenediamine, water 1 kilogram, B8905 0.5 kilogram.Put the weighed polyether polyol and polymer polyol material into the reactor and stir, then add the weighed cross-linking agent, catalyst, blowing agent, stabilizer, at normal temperature Stir for combined reaction, stir for 3.5 hours, take it out for inspection, meet the process parameters, and emit satisfactory foam, that is, the qualified product of component A is obtained, take it out of the reaction kettle and put it into a barrel for storage.

[0041] Prep...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Tear strengthaaaaaaaaaa
Login to view more

Abstract

The microporous polyurethane elastomer composition material suitable for insole consists of one component A and one component B in the weight ratio of 100 to 60-80. The component A consists of polyether polyol, polymer polyol, cross-linking agent, foam stabilizer, foaming agent and catalyst; and the component B is pre-polymer of polyether polyol and isocyanate. When it is used, the two components are mixed in the said weight ratio at normal temperature to form microporous polyurethane elastomer. The normal temperature production process of insole is simple and has easy operation, no waste, stable product quality and low production cost.

Description

technical field [0001] The invention belongs to a polyurethane microporous elastomer composite material, in particular to a polyurethane microporous elastomer composite material suitable for insoles and a preparation method thereof. Background technique [0002] At present, the shoe industry has become an important market for polyurethane products. China has a large population, and polyurethane raw materials for shoes have great potential for development. In recent years, many manufacturers of high-end sports shoes have produced the insole (also known as the inner bottom) as an independent unit, and the molding density of the insole is required to be 0.2-0.3g / cm 3 , and requires stable dimensions, high strength, good surface crust, and no defects. Now on the market, most of the insoles are polyester type, and a small amount of ordinary high-activity polyether type is used. Some properties of polyester insoles, such as abrasion resistance and tear resistance, are superior ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L75/08C08J9/04A43B17/14
Inventor 孙清峰李健栾森于鹏程
Owner SHANDONG INOV POLYURETHANE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap