Precisely carving fatlute and method for preparing same

A kind of oil sludge and fine carving technology, applied in the field of sculpture oil mud and preparation, it can solve the problems of the texture particles are not fine and cannot be softened and modified at room temperature, etc., and achieve the effect of hard texture, strong plasticity and high precision.

Inactive Publication Date: 2008-05-14
东莞市汇欣工贸有限公司
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to overcome the technical deficiencies of the existing Jingdiao oil sludge, which are not fine in texture particles and cannot be softened and modified at room temperature, the purpose of the present invention is to provide a Jingdiao with hard and fine texture at room temperature, which can be finely carved, can be softened at low temperature, and does not shrink. Sludge; the purpose of the present invention is also to provide its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Embodiment 1: A kind of plastic sculpture oil mud provided in this embodiment, comprises the raw material component of following weight ratio: (unit: kg) paraffin wax 30~50, soft wax 8~20, Vaseline 4~12, calcium carbonate 60 ~130, toner 0.2~0.8, and the rest are trace moisture and impurities. Specifically, it includes: 30kg of paraffin wax, 8kg of soft wax, 4kg of vaseline, 60kg of calcium carbonate, 0.2kg of toner, and the rest is trace water and impurities.

[0021] Its preparation method that present embodiment provides, comprises the steps:

[0022] 1. Weigh each raw material in proportion;

[0023] 2. Put the weighed paraffin wax, soft wax, and vaseline into the reaction kettle, and heat to 80°C-140°C;

[0024] 3. After the raw materials in step (2) are dissolved, add calcium carbonate and stir until there is no fine powder;

[0025] 4. Then add the toner into the reaction kettle, and stir until the toner completely dissolves into the raw materials;

[0026] 5....

Embodiment 2

[0029] Embodiment 2: The plastic sculpture oil mud provided in this embodiment and its preparation method are the same as in Example 1, the difference being that the weights of the components of the plastic sculpture oil mud are changed in turn: 38 kg of paraffin wax, 12 kg of soft wax, Vaseline 6kg, calcium carbonate 90kg, toner 0.4kg, the rest is trace water and impurities.

Embodiment 3

[0030] Embodiment 3: the plastic sculpture sludge provided in this embodiment and its preparation method are the same as those in Examples 1 and 2, the difference being that the weights of the components of the plastic sculpture sludge are changed in sequence: paraffin wax 50kg, soft wax 20kg, Vaseline 12kg, Calcium Carbonate 130kg, Toner 0.8kg, the rest is trace moisture and impurities.

[0031] The plastic sculpture clay product provided in the above examples has a hardness coefficient of 60±5 after drying; a fineness of more than 1200 mesh; a shrinkage rate of one thousandth; and a softening temperature of 40-45°C.

[0032] The new product made by the present invention—thin slice plastic sculpture oil clay can be kneaded with hand temperature, and the thick block is very hard after shaping. If it is reshaped, it can be packed in heat-resistant plastic bags, soaked in hot water or packed Put it into the electric cooker in the cylinder to soften. The electric cooker is only p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Softening temperatureaaaaaaaaaa
Login to View More

Abstract

The invention discloses a carved oil sludge and a preparation method thereof, which is prepared from the following raw materials in parts by weight: paraffin wax 30-50, soft wax 8-20, vaseline 4-12, calcium carbonate 60-130, toner 0.2-0.8 , and the rest are trace moisture and impurities. The invention also discloses a preparation method thereof, the steps of which are: weighing each raw material in proportion; putting paraffin, soft wax, and vaseline into a reaction kettle for heating; adding calcium carbonate after the raw materials are melted, and stirring evenly in the reaction kettle until There is no fine powder for this purpose; add toner and stir until the toner is completely dissolved in all raw materials; remove from the fire, pour the obtained slurry into a container for cooling. The texture of the invention is hard and delicate at normal temperature, can be finely carved, can be softened at a slight temperature, does not stick to hands, and does not shrink.

Description

Technical field: [0001] The invention relates to a sculpture material, in particular to a sculpture clay and a preparation method. Background technique: [0002] Soft pottery clay, finely carved oil clay, and colored clay products are mainly used in the existing handicraft industry prototype making, art teaching, model making, and mold prototype making. Some oil sludge will shrink after drying, and the requirements for this characteristic are particularly important when making mold prototypes. As for finely carved oil clay, some texture particles of existing finely carved oil clay are not fine, and the surface of the sculpture is rough. And some are not easy to soften and shape or repair at normal temperature after drying, especially not suitable for teaching and learning. Invention content: [0003] In order to overcome the technical deficiencies of the existing Jingdiao oil sludge, which are not fine in texture particles and cannot be softened and modified at room temp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L91/06C08K5/00C08K3/26
Inventor 冯诗荣
Owner 东莞市汇欣工贸有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com