Disk shearing blade and method for manufacturing the same

A manufacturing method and scissor blade technology, which are applied in the direction of manufacturing tools, knives for shearing machine devices, shearing devices, etc., can solve the problems of rapid passivation, uneven wear, low hardness of disc scissors, and achieve good Wear resistance and deformation resistance, improve strength and fatigue resistance, reduce the effect of notch sensitivity

Active Publication Date: 2008-05-14
BAOSHAN IRON & STEEL CO LTD +1
View PDF2 Cites 41 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0013] Disc scissors blades are less hard and wear-resistant due to the absence of other strong carbide forming elements; or
[0014] In order to improve the hardness of the blade and meet the requirements of blade use, the quenching temperature and tempering temperature during quenching and tempering heat treatment, and the quenching temperature and tempering temperature during final heat treatment have to be reduced in the production process, resulting in the thermal deterioration of its structure and hardness. Poor stability and retention, only applicable to the operating conditions of cold disc shears; or
[0015] Due to the lack of wear-resistant alloy carbide phase, the wear resistance and scratch resistance of the material are poor, so when the disc scissors are used to cut high-strength thick steel plates, they are prone to edge flanging, chipping, and failure. Uniform wear and fluting, rapid passivation phenomena, resulting in frequent downtime for blade replacement; or,
[0016] The diameter of the disc scissors is small, about 300mm, generally only used for cutting ordinary thin steel plates, not suitable for cutting high-strength thick steel plates, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-6

[0044] At first, the disc scissors blade material of the present invention was made respectively according to the chemical composition shown in Table 2.

[0045] Table 2 Chemical composition of disc scissors blade material (Wt.%)

[0046] C

Si

mn

Ni

Cr

Mo

Nb

V

P

S

Example 1

0.70

1.20

0.50

1.50

4.50

0.50

0.80

0.30

0.015

0.008

Example 2

0.50

1.00

0.35

1.20

5.10

1.40

0.50

1.00

0.015

0.008

Example 3

0.55

0.50

0.20

1.00

5.50

2.00

0.10

1.50

0.015

0.008

Example 4

0.55

0.70

0.50

1.30

5.20

1.00

0.40

0.80

0.015

0.008

Example 5

0.40

0.80

0.40

1.40

4.00

0.80

0.30

1.20

0.015

0.008

Example 6

0.5...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

A disc scissors blade and its manufacturing method, the composition weight percentage of the material of the disc scissors blade is: C: 0.40-0.70%, Si: 0.50-1.2%, Mn: 0.20-0.50%, Ni: 1.00-1.50% %, Cr: 4.00-6.00%, Mo: 0.50-2.00%, V: 0.30-1.50%, Nb: 0.10-0.80%, P≤0.02%, S≤0.02%. The method introduces an electroslag remelting process into a common manufacturing method of disc shears, and increases the temperature of quenching and tempering heat treatment and final heat treatment. The disc scissors have good wear resistance and deformation resistance, and are suitable for slitting or trimming hot-rolled high-strength thick steel plates. In addition, the disc shear blade of the present invention also has a good use effect on disc shears in other similar working conditions, and can also be applied to disc shears for stripping or edge trimming of cold-rolled strip steel, and also has a promotional effect on non-ferrous metal disc shears. value and application prospects.

Description

technical field [0001] The present invention relates to a metallurgical machinery blade and its manufacturing method. Specifically, the present invention relates to a disc scissors blade and its manufacturing method. The disc scissors blade of the present invention is suitable for slitting hot-rolled high-strength thick steel plates. or trimming. Background technique [0002] With the rapid development of my country's railway, bridge, construction, petroleum, automobile, and home appliance industries, the proportion of high-strength hot-rolled commercial steel products continues to increase. These steel products include: pipeline steel, automobile girder plates, high-strength container plates, and high-strength engineering machinery. Steel, tool steel, knife die saw blade steel and other series of varieties. [0003] Due to the high internal stress of the incoming high-strength steel plate, the poor shape and section quality, the shearing production is difficult, and it is e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/48B23D35/00B23D19/00C22C33/04C21D1/26C21D1/18C21D9/22C21D11/00
Inventor 孙大乐张四华杨征范群张健姚利松卢振鸣张新猷张军戴奎石张卫龙
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products