Method for preparing WC-Co series nano composite hard alloy powder
A kind of cemented carbide and nano-composite technology, which is applied in the field of ultrafine WC-Co series cemented carbide powder preparation
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0031] Embodiment 1, preparation of WC-20Co nanocomposite cemented carbide powder:
[0032] Using the above-mentioned corona discharge plasma-assisted high-energy ball mill, the total volume of selected balls accounts for 75% of the volume of the ball mill tank, wherein the number of balls with a diameter of 22mm accounts for 15% of the total number of balls, and the number of balls with a diameter of 18mm accounts for 75% of the total volume of the ball mill. 75% of the number of grinding balls, the number of grinding balls with a diameter of 10mm accounts for 10% of the total number of grinding balls, and the loose volume of W, C, and Co raw materials to be processed accounts for 130% of the gap between the grinding balls.
[0033] Preparation of WC-20Co nanocomposite cemented carbide powder comprises the following steps:
[0034] (1) Install the front cover plate and electrode rod of the ball milling tank, and connect the ball milling tank and electrode rod to the positive ...
Embodiment 2
[0039] Embodiment 2, preparation of WC-10Co nanocomposite cemented carbide powder:
[0040] Using the above-mentioned corona discharge plasma-assisted high-energy ball mill, the total volume of the selected balls accounts for 70% of the volume of the ball mill tank, wherein the number of balls with a diameter of 20mm accounts for 10% of the total number of balls, and the number of balls with a diameter of 15mm accounts for 70% of the total volume of the ball mill. 80% of the number of grinding balls, the number of grinding balls with a diameter of 10mm accounts for 10% of the total number of grinding balls, and the loose volume of W, C, and Co raw materials to be processed accounts for 60% of the gap between the grinding balls.
[0041] Preparation of WC-10Co nanocomposite cemented carbide powder comprises the following steps:
[0042] (1) Install the front cover plate and electrode rod of the ball milling tank, and connect the ball milling tank and electrode rod to the positi...
Embodiment 3
[0047] Embodiment 3, preparation of pure WC nanocomposite cemented carbide powder:
[0048] Using the above-mentioned corona discharge plasma assisted high-energy ball mill, the process conditions for processing W, C, and Co are basically the same as those for preparing WC-20Co cemented carbide. The atomic ratio of the high-quality alloy components is added, in which 5% of carbon is added, and Co is not added at this time; the gas medium to be filled is N2; the voltage of the plasma power supply is 10KV, and the frequency is 5KHz; the synthesis temperature is 1100°C, and the pressure of the heat source is 0.1MPa. The product is pure WC nanocomposite cemented carbide powder.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com