Imitating stone ceramic tile producing method

A manufacturing method and ceramic tile technology, which is applied in the field of building decoration materials, can solve the problems of unsatisfactory antifouling effect and poor color variety compared with ceramic tiles, and achieve high gloss and antifouling ability, good decorative effect, and high compressive strength. big effect

Inactive Publication Date: 2008-06-11
罗永杰
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the existing polished tiles have fine texture, good decorative effect, texture, anti-fouling, wear resistance, and gloss parameters are relatively ideal, their three-dimensional effect is not as good as that of natural stone. Although natural stone has a stronger three-dimensional effect than ceramic tiles, its The variety of designs and colors is inferior to ceramic tiles, and the antifouling effect is not ideal, and because it is generally radiant, customers have concerns about their choice

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Imitating stone ceramic tile producing method
  • Imitating stone ceramic tile producing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] The present invention will be described in further detail below in conjunction with specific embodiment (billet unit is weight percent):

[0026] surface

[0027]

[0028] Continuation

[0029]

[0030] The manufacturing process of the imitation stone tiles is as follows: batching according to the foregoing embodiments → ball milling → slurry → sieving and stale, iron removal → spray drying → powder → stale homogenization → brick adobes in rows → drying → printing → firing (surface temperature , At the same time, the bottom temperature is 5-10°C lower than that of ordinary micro-powder bricks, and the quenching section is controlled between 610-620°C)→polishing→grading→packaging→storage.

[0031] Due to the combination of low-temperature Yulinglong material and high-temperature material (the temperature difference is 100 degrees Celsius), some temperature properties can be changed by selecting reasonable additives and mineralizers during firing to ensure that the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Disclosed is a method for preparing granolithic ceramic tile and the chemical component of main raw material is that Fe2O3 0.12-1.28%, MgO 0.01-0.2%, CaO 0.01-1.46%, TiO2 0.04-0.68%, Al2O3 15.55-32.25%, SiO2 52.03-74.52%, K2O 0.07-5.34% and Na2O 0.16-8.88%, wherein the surface temperature and bottom temperature of the burnt temperature is reduced by 5-10 DEG C compared with ordinary micronized brick, the quench segment is controlled between 610 and 620 DEG C, the burnt temperature is 1195-1205 DEG C, and the burnt period is 60-90 min. The invention utilizes contrast of powder and high white powder of various colors to form deep perspective effects of various laminated shapes by burden distribution according to different programs.

Description

technical field [0001] The invention relates to a method for manufacturing building decoration materials, in particular to a method for manufacturing imitation stone tiles. Background technique [0002] With the continuous development of building decoration materials at home and abroad, people have higher and higher requirements for the decoration effect of decoration materials. Not only high-end and novelty are required, but also the decoration effect should be close to natural materials. The product. In the existing technology, ceramic decorative tiles have become the object of choice for customers and consumers due to their extremely low water absorption, good wear resistance, small shrinkage deformation, high strength, anti-fouling, anti-skid, and rich decorative effects. The more it is praised and favored by customers, and it has a long-term and broad market. However, due to the fact that customers have more and more perfect requirements for tiles in the existing tech...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/14C04B35/622
Inventor 罗永杰
Owner 罗永杰