Strong fibre polishing wheel

A technology of strong fibers and polishing wheels, applied in abrasives, metal processing equipment, manufacturing tools, etc., can solve the problems of increasing production and processing costs, low gloss, etc., and achieve the effects of improved durability, good flexibility, and obvious effects.

Inactive Publication Date: 2008-07-09
郑州新安华砂轮有限公司
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the currently used polishing wheels can achieve a certain degree of smoothness on the surface of metal or non-metallic components, the gloss is low. For non-ferrous metal components that need to maintain their original colors, mirror grinding machines are often used for polishing and polishing. Production and processing costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] The powerful fiber polishing wheel of the present invention is prepared from the following mixture and fiber material in proportions by weight:

[0018] a. Mixing ratio:

[0019] Natural latex: 100 parts; Zinc oxide: 0.5 parts; Anti-aging agent DNP: 0.2 parts;

[0020] Antiaging agent 264: 0.8 parts; Casein: 0.3 parts; Potassium hydroxide: 0.05-0.1 parts;

[0021] Lanolin: 0.5 parts; Accelerator PX: 1 part; Sulfur: 1 part; Sand: 135.655 parts;

[0022] B, the proportioning by weight of fiber material and described mixture is: 1: 7-8;

[0023] c. Preparation method:

[0024] In the first step, zinc oxide, anti-aging agent DNP, anti-aging agent 264, casein, potassium hydroxide, lanolin, accelerator PX, sulfur, and sand are evenly mixed together for later use;

[0025] In the second step, the material obtained in the first step is added to the natural rubber latex and stirred evenly;

[0026] In the third step, the material obtained in the second step and the fiber ma...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses a fibre polishing wheel, which is prepared by the following mixture and fibre material: (a) the proportions of the mixture: 100 portions of natural latex, 0.5 portions of zinc oxide, 0.2 portions of age inhibitor DNP, 0.8 portions of age inhibitor 264, 0.3 portions of casein, 0.05 to 0.1 portions of potassium hydroxide, 0.5 portions of lanoline, 1 portion of accelerant PX, 1 portion of sulfur and 135.655 portions of sand; (b) the weight portion proportion of the fibre material and the mixture: 1 : 7 to 8; (c) the preparation method: (1) the zinc oxide, the age inhibitor DNP, the age inhibitor 264, the casein, the potassium hydroxide, the lanoline, the accelerant PX, the sulfur and the sand are uniformly mixed for later use; (2) The material of the first step is uniformly mixed with natural latex; (3) the material of the second step is uniformly mixed with the fibre material and then is squeezed in a rolling machine, so that the material is uniformly immerged into fibre; (4) the material-immerged fibre of the third step is rolled up and placed into a mould, which is then put into a thermotank and heated, and finally, after vulcanization, a finished product is obtained. The present invention has the advantage of that the polishing effect is obvious.

Description

technical field [0001] The invention relates to a powerful fiber polishing wheel for metal and non-metal products. Background technique [0002] In order to ensure the smoothness of the surface of metal and non-metal components, it is often necessary to polish the surface to meet the process requirements of a process. For non-ferrous metals, such as stainless steel products, alloy aluminum products, copper products, etc., the finished product needs to be polished to achieve a certain gloss because the original color of the metal should be maintained. Although the currently used polishing wheels can achieve a certain degree of smoothness on the surface of metal or non-metallic components, the gloss is low. For non-ferrous metal components that need to maintain their original colors, mirror grinding machines are often used for polishing and polishing. Production and processing costs. Contents of the invention [0003] The object of the invention is to provide a powerful fi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B24D3/20B24D3/34
Inventor 王道敏
Owner 郑州新安华砂轮有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com