Sponge bonding rubber as well as preparation method and method for avoiding foaming of rubber shoes sponge
A technology of adhesive glue and sponge glue, which is applied in the direction of shoemaking machinery, adhesive types, and bonded shoe parts, etc., can solve problems such as the quality of sponge foam in rubber shoes, and achieve the effect of solving the problem of adhesive delamination
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0054]Embodiment 1: raw materials are taken in proportion: rubber 1000g, sulfur 25g, vulcanization accelerator DS 50g, nano zinc oxide (vulcanization activator) 80g, clay (filler) 1850g and composite resin DS-B (tackifying resin) 450g . First, take the rubber and carry out mastication on the XK-400 open mill. The temperature of the rollers is 40-50°C, the roller distance is 0.8mm, and the roller distance is passed 3-4 times, and then the rubber is wrapped on the open mill with a roller distance of 9-10mm. The roller removes air bubbles, so that the plasticity of the rubber reaches 0.45, and then the plasticized rubber is obtained, and then the plasticized rubber is added to the internal mixer, and then the vulcanization accelerator DS, nano-zinc oxide, clay, and composite resin DS-B are added in sequence, and after mixing Mix at 90-100°C until the plasticity is 0.4-0.5 to obtain the sponge adhesive. Tested on a steam-heated flat vulcanizer with a temperature of 143±1°C and a ...
Embodiment 2
[0056] Embodiment 2: raw materials are taken in proportion: rubber 800g, sulfur 20g, vulcanization accelerator DM 60g, stearic acid (vulcanization active agent) 90g, clay (filler) 2100g and composite resin DS-B (tackifying resin) 400g , Take the rubber and masticate it on the internal mixer for 5-5.5min. The conditions of the internal mixer are: the temperature of the internal mixing room is 90-120°C, the pressure of the internal mixing room is 0.2Mpa, and the rotor speed of the internal mixer is 1440r / min, so that the plasticity can reach 0.4, then add vulcanization accelerator DS, stearic acid, clay, and composite resin DS-B in sequence, mix and refine at 100-120°C for 4-6 minutes to obtain the sponge adhesive.
[0057] The gluing process is as described in Example 1.
Embodiment 3
[0058] Embodiment 3: raw material is taken in proportion: rubber 30kg, sulfur 0.75kg, vulcanization accelerator DM 1.5kg, stearic acid (vulcanization activator) 2.4kg, pottery clay (filler) 55.5kg and composite resin DS-B (enhancement agent) Adhesive resin) 15kg, masticate the rubber to make its plasticity reach 0.5, then add vulcanization accelerator DM, stearic acid, pottery clay, and composite resin DS-B in sequence, mix and knead according to the conventional process to obtain the sponge adhesive glue.
[0059] The gluing process is as described in Example 1.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap