Ultra-low carbon hot rolling weather-resisting steel with yield strength more than 450MPa

A yield strength, ultra-low carbon technology, applied in the field of low-alloy steel manufacturing, can solve the problems of poor mechanical properties, poor atmospheric corrosion resistance, and high C content, and achieve the effects of excellent mechanical properties, simple chemical composition, and improved corrosion resistance.

Inactive Publication Date: 2008-08-06
WUHAN IRON & STEEL (GROUP) CORP
View PDF3 Cites 38 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The present invention aims at the shortcomings of existing weathering steels such as poor mechanical properties, poor atmospheric corrosion resistance, and high C content. The invention provides an ultra-low carbon hot-rolled weathering steel with a yield

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultra-low carbon hot rolling weather-resisting steel with yield strength more than 450MPa
  • Ultra-low carbon hot rolling weather-resisting steel with yield strength more than 450MPa
  • Ultra-low carbon hot rolling weather-resisting steel with yield strength more than 450MPa

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] According to the above production process, steel 1 was produced, wherein the chemical composition of steel 1 is shown in 1 in Table 1, the mechanical properties of steel 1 are shown in 1 in Table 2, and the atmospheric corrosion resistance results of steel 1 are shown in 1 in Table 3.

Embodiment 2

[0032] According to the above production process, steel 2 is produced, wherein the chemical composition of steel 2 is shown in 2 in Table 1, the mechanical properties of steel 2 are shown in 2 in Table 2, and the atmospheric corrosion resistance results of steel 2 are shown in 2 in Table 3.

Embodiment 3

[0034] According to the above production process, steel 3 is produced, wherein the chemical composition of steel 3 is shown in 3 in Table 1, the mechanical properties of steel 3 are shown in 3 in Table 2, and the atmospheric corrosion resistance results of steel 3 are shown in 3 in Table 3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Yield strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention provides ultra-low carbon hot rolling weathering steel whose yield strength is more than 450MPa aiming at the defects of existing weathering steel that the mechanical property and the atmospheric corrosion resistance are bad and the C content is over high, which is composed of components with following weight percent: C 0.01-0.05%, Si 0.10-0.40%, Mn 1.50-1.90%, P<=0.02%, S<=0.010%, Cu 0.15-0.55%, Cr 0.20-0.80%, Ni 0.10-0.50%, Mo 0.05-0.50, Nb 0.01-0.05% and Ca 0.0010-0.0020, and allowance is Fe and unavoidable impurity. The strength grade of the steel of the invention is higher than that of traditional steel and the steel has excellent low temperature impact toughness, welding performance and atmospheric corrosion resistance, and adopts ultra-low carbon design, which is beneficial for extending and applying.

Description

technical field [0001] The invention relates to an ultra-low-carbon hot-rolled weathering steel, specifically a weathering steel with a yield strength of 450MP, low-temperature toughness, good cold formability and weldability, and excellent atmospheric corrosion resistance, which belongs to low alloy steel manufacturing field. Background technique [0002] Weathering steel is a low-carbon low-alloy steel, which is widely used in the manufacture of railway vehicles, transmission towers, offshore platforms and long-term outdoor engineering components. At the beginning of this century, the development of my country's railway vehicle manufacturing, transmission towers, offshore platforms and long-term outdoor engineering components put forward high-strength requirements for weathering steel. Especially in order to meet the development requirements of high-speed and heavy-duty railway transportation in my country, it is necessary to increase the strength of weathering steel, red...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/58
Inventor 刘志勇陈吉清陈邦文胡敏宋育来
Owner WUHAN IRON & STEEL (GROUP) CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap