Metal ink

A metal ink and metal pigment technology, applied in the direction of ink, pigment slurry, fibrous filler, etc., can solve the problems of difficulty in see-through latent image, unidentifiable pattern, high precision, etc., achieve strong anti-counterfeiting performance, improve aesthetics, latent printing easy effect

Active Publication Date: 2008-08-13
CHINA BANKNOTE PRINTING & MINTING
View PDF0 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This kind of latent image cannot be recognized as a complete pattern when viewed under normal light on one side, and the pattern needs to be separated during design. A special gravure printing machine is required for printing, and the printing overprinting accuracy is high to achieve perspective Hiding is more difficult

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metal ink

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Embodiment 1: metallic ink comprises metal pigment, binder, filler, surfactant and polyethylene wax, and wherein binder is alkyd resin oil, high acid value phenolic resin oil, pure phenolic resin oil, and filler is vapor phase dioxide Silicon, transparent calcium carbonate.

[0030] The composition and weight percentage of metallic ink are as follows:

[0031] Flake silver powder 15%

[0032] Alkyd Oil 12%

[0033] High acid value phenolic resin oil 25%

[0034] Pure Phenolic Oil 8%

[0035] Fumed silica 3%

[0036] Transparent Calcium Carbonate 19%

[0037] Surfactant 5.5%

[0038] Polyethylene Wax 8%

[0039] Mineral oil 4%

[0040] Desiccant 0.5%

[0041] The production of metal ink is as follows:

[0042] 1. According to the above formula, weigh the alkyd resin oil, high acid value phenolic resin oil, pure phenolic resin oil, fumed silica, transparent calcium carbonate, surfactant, and polyethylene wax, mix them evenly and use three The ink roll is rolled...

Embodiment 2

[0045] Embodiment 2: The composition and percentage content of the metal ink used to print the lines of the see-through latent image and the base pattern on one side of the carrier are as follows:

[0046] Flake aluminum powder 20%

[0047] Alkyd Oil 15%

[0048] High acid value phenolic resin oil 20%

[0049] Pure Phenolic Oil 10%

[0050] Fumed silica 5%

[0051] Transparent Calcium Carbonate 15%

[0052] Surfactant 6.7%

[0053] Polyethylene wax 6%

[0054] Mineral oil 2%

[0055] Desiccant 0.3%

[0056] The method and structure of the metallic ink for making a single-sided see-through latent image printed with the metallic ink are as in Example 1.

Embodiment 3

[0057] Embodiment 3: The composition and percentage content of the metal ink used to print the lines of the see-through latent image and the base pattern on one side of the carrier are as follows:

[0058] Flake copper powder 24%

[0059] Alkyd Oil 10%

[0060] High acid value phenolic resin oil 24%

[0061] Pure Phenolic Oil 8%

[0062] Fumed silica 3%

[0063] Transparent Calcium Carbonate 16%

[0064] Surfactant 5.6%

[0065] Polyethylene wax 6%

[0066] Mineral oil 3%

[0067] Desiccant 0.4%

[0068] The method and structure of the metallic ink for making a single-sided see-through latent image printed with the metallic ink are as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a metallic printing ink, relating to an anti-counterfeiting printing ink which can form an anti-counterfeiting latent image by single-face printing has better anti-counterfeiting performance, wherein, the latent image can be identified by people without using special apparatus. The percentage of weight of each component is as following: 15 to 25% metallic paint, 10 to 15% high acid valence phenolic resin oil, 8 to 10% pure phenolic resin oil, 3 to 5% vapor phase silica, 15 to 20% transparent calcium carbonate, 5 to 7% surfactant, 6 to 8% polyethylene wax, 2 to 4% mineral oil, 0.3 to 0.5% drier, wherein the metallic paint is any one of the flake silver powder, aluminium powder, copper powder, or the mixture of the two or three components. The invention is applicable for single-face printing anti-counterfeiting perspective latent image on various carriers, such as different securities or the carriers of plastic, rubber and glass with certain transparence.

Description

technical field [0001] The invention relates to an ink for anti-counterfeiting printing, in particular to a metal ink containing metal pigments for printing anti-counterfeiting latent images. Background technique [0002] Latent image is an anti-counterfeiting technology that hides specific patterns at normal viewing angles and observes and recognizes them under specific observation conditions. It is a technology widely used in the field of anti-counterfeiting printing. It has concealed anti-counterfeiting and easy identification. features. [0003] At present, the most widely used latent image technology is to use colorless fluorescent ink printing, and the printed pattern is hidden under visible light and clearly visible under ultraviolet light. But this kind of latent image requires the help of a specific instrument (ultraviolet light source), and the technical threshold for counterfeiting is relatively low, which has been broken by counterfeiters, and the effectiveness ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/10C09D17/00C09C1/62C09D11/50
Inventor 李军黄小义房晓龙潘东王自森邱燕新张勇詹刚
Owner CHINA BANKNOTE PRINTING & MINTING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com