Non-phenols overlay film sand and producing method thereof

A technology of coated sand and silica sand, which is used in foundry molding equipment, molds, cores, etc., can solve the problems of lowering the melting point of coated sand, influence of the fluidity of coated sand, and increase of flue gas, etc. Good stability and the effect of reducing smoke

Inactive Publication Date: 2008-08-27
TIANJIN YABU NEW TECH
View PDF0 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But their addition will reduce the melting point of the coated sand, which will affect the fluidity of the ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-phenols overlay film sand and producing method thereof
  • Non-phenols overlay film sand and producing method thereof
  • Non-phenols overlay film sand and producing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Embodiment 1: a kind of phenol-free coated sand is characterized in that it is made of silica sand, phenolic resin, urotropine, calcium stearate and polyethylene polyamine; wherein in every 100 kilograms of silica sand, add phenolic resin 2 kg, 0.3 kg of urotropine, 0.2 kg of calcium stearate, and 0.08 kg of polyethylene polyamine.

[0016] A kind of production method of above-mentioned phenol-free coated sand is characterized in that it is made of following steps:

[0017] (1) Heat the silica sand to 150°C;

[0018] (2) Add phenolic resin and polyethylene polyamine in proportion to the silica sand obtained in step (1), and mix uniformly;

[0019] (3) in the product that step (2) obtains, add the aqueous solution of urotropine in proportion, mix homogeneously;

[0020] (4) calcium stearate is added in proportion to the product obtained in step (3), mixed and broken;

[0021] (5) Sieve to obtain phenol-free coated sand.

[0022] The molecular formula of polyethylene ...

Embodiment 2

[0026] Embodiment 2: a kind of phenol-free coated sand is characterized in that it is made of silica sand, phenolic resin, urotropine, calcium stearate and polyethylene polyamine; wherein in every 100 kilograms of silica sand, add phenolic resin 3 kg, 0.4 kg of urotropine, 0.3 kg of calcium stearate, and 0.09 kg of polyethylene polyamine.

[0027] A kind of production method of above-mentioned phenol-free coated sand is characterized in that it is made of following steps:

[0028] (1) Heat the silica sand to 160°C;

[0029] (2) Add phenolic resin and polyethylene polyamine in proportion to the silica sand obtained in step (1), and mix uniformly;

[0030] (3) in the product that step (2) obtains, add the aqueous solution of urotropine in proportion, mix homogeneously;

[0031] (4) calcium stearate is added in proportion to the product obtained in step (3), mixed and broken;

[0032] (5) Sieve to obtain phenol-free coated sand.

[0033] The molecular formula of polyethylene ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A phenol-free coated sand is characterized in that the coated sand is prepared from silicon sand, phenol-formaldehyde resin, urotropine, calcium stearate and macromolecular substances containing amino groups. The preparation method comprises the following steps of: (1) heating the silicon sand to 140 to 160 DEG C; (2) adding the phenol-formaldehyde resin and additives; (3) adding aqueous solution of the urotropine; (4) adding the calcium stearate; and (5) sieving to obtain the phenol-free coated sand. The phenol-free coated sand has the advantages that a material for reducing the content of free phenols and improving sand core performance is the reaction resultant of the macromolecular substances containing amino groups and the free phenols, which is an intermediate substance with a certain chemical reaction activity and can crosslink with each other to form macromolecules in hot curing reaction for core manufacture or formation. The macromolecules have infusibility and melting resistance, good thermal stability, no phenol volatilization and less production of smoke, and can increase the strength and the toughness of sand core or sand mold and improve the melting point of the coated sand by a certain degree, thus greatly improving the performance of the sand core.

Description

(1) Technical field: [0001] The invention relates to a modeling material and a production method thereof, in particular to a phenol-free coated sand and a production method thereof. (two) background technology: [0002] At present, before modeling and core making, the surface of the sand has been covered with a layer of solid resin film, also known as shell sand or core sand. It was originally a kind of thermosetting resin sand, which was invented by Dr. Knin of Germany in 1944. The process is to mechanically mix powdery thermosetting phenolic resin with raw sand, and solidify when heated. It has been developed into a coated sand made of thermoplastic phenolic resin plus a latent curing agent such as urotropine and a lubricant such as calcium stearate through a certain coating process. When the coated sand is heated, it is coated on the surface of the sand grains. The resin melts, and under the action of the methylene decomposed from urotropine, the molten resin rapidly tr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22C1/10C08L61/06C08K5/17C08K5/098C08K3/34
Inventor 时伟钱进
Owner TIANJIN YABU NEW TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap