Multifunctional environment protection type artificial board and method of producing the same

A wood-based panel and environment-friendly technology, applied in the field of wood-based panels and their preparation, can solve problems such as single function, and achieve the effect of improving the use function.

Active Publication Date: 2008-09-24
INST OF WOOD INDUDTRY CHINESE ACAD OF FORESTRY
View PDF1 Cites 31 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to solve the technical problem of the single function of the wood-based panel material in the prior art, and provide a multi-functional environment-friendly wood-based panel and its preparation method. Indoor air, the health function of degrading formaldehyde, toluene, nitrogen oxide and other harmful gases

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] Prepare 12mm thick MDF as follows:

[0046] 1) Prepare materials according to the following weight ratio:

[0047] Poplar fiber (dry) 100kg

[0048] Phenolic resin glue (solid content) 10kg

[0049] Tourmaline Powder 8kg

[0050] Titanium dioxide powder 1kg

[0051] Activated carbon powder 5kg

[0052] Ag 2 O (antibacterial agent) powder 1kg

[0053] 2) Mix all the poplar fibers with the phenolic resin glue and stir evenly;

[0054] 3) Mix the poplar fiber mixed with phenolic resin glue with all tourmaline powder, titanium dioxide powder, activated carbon powder and antibacterial agent Ag 2 O micropowder mixing, stirring evenly;

[0055] 4) Paving and pre-pressing of the slab: paving the mixture into a slab, and pre-pressing with a pressure of 1.6MPa for 20s.

[0056] 5) Hot-pressing the slab: the technological conditions of hot-pressing are pressure 2.5 MPa, temperature 180° C., and hot-pressing time 20 s / mm.

[0057] 6) After hot pressing, it is cooled and f...

Embodiment 2

[0065] Follow the steps below to prepare 12mm thick particleboard:

[0066] 1) Prepare materials according to the following weight ratio:

[0067] Hemp shavings (dry) 100kg

[0068] Urea-formaldehyde resin glue (solid content) 15kg

[0069] Tourmaline Powder 3kg

[0070] Titanium dioxide powder 10kg

[0071] Activated carbon powder 2.5kg

[0072] ZnO (antibacterial agent) powder 5kg

[0073] 2) Mix all the urea-formaldehyde resin glue with all the tourmaline micropowder, titanium dioxide micropowder, activated carbon micropowder and antibacterial ZnO micropowder, and stir evenly;

[0074] 3) Add the uniformly mixed urea-formaldehyde resin glue, tourmaline powder, titanium dioxide powder, activated carbon powder and antibacterial agent ZnO powder into pine wood shavings and mix them evenly.

[0075] 4) Paving and pre-pressing of the slab: paving the mixture into a slab, and pre-pressing with a pressure of 1.6MPa for 20s.

[0076] 5) Hot-pressing the slab: the technologic...

Embodiment 3

[0085] Prepare 12mm thick fibreboard as follows:

[0086] 1) Prepare materials according to the following weight ratio:

[0087] A: The surface layer and the bottom layer are prepared according to the following proportions

[0088] Cotton stalk fiber (dry) 100kg

[0089] Urea-formaldehyde resin glue (solid content) 11kg

[0090] Tourmaline powder 10kg

[0091] Titanium dioxide powder 5kg

[0092] Activated carbon powder 1kg

[0093] CuO (antibacterial agent) powder 2.5kg

[0094] B: core material preparation:

[0095] Cotton stalk fiber (dry) 100kg

[0096] Urea-formaldehyde resin glue (solid content) 11kg

[0097] 2) Mix the urea-formaldehyde resin glue of the surface layer and the bottom layer with all tourmaline micropowders, titanium dioxide micropowders, activated carbon micropowders and antibacterial CuO micropowders, and stir evenly;

[0098] 3) the urea-formaldehyde resin glue mixed with tourmaline micropowder, titanium dioxide micropowder, activated carbon mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a multifunctional and environmental protective hard board composed of fibre or paring, and a preparation method thereof. In the production process of the hard board, appropriate quantity of functional material is mixed in the plant fibre or in the paring; the functional material contains tourmaline powders; wherein, proportioning by weight of the plant fibre or the plant paring and the tourmaline powder is 100:0.5 to 10; thereby the prepared hard board has manifold environmental protective functions such as anion releasing, far infrared ray emission, antibiosis, room air purifying, degradation of noxious gas (like formaldehyde, toluene nitrogen oxide, etc.), etc.

Description

technical field [0001] The invention relates to an artificial board, in particular to an artificial board made of fibers or shavings and a preparation method thereof. Background technique [0002] With the continuous improvement of people's living standards, the awareness of environment and health is gradually increasing, and people will pay more and more attention to green materials and environmentally friendly products. Health, longevity and comfort have become the highest goals pursued by people. Environmental protection, health and antibacterial products came into being and developed rapidly. Wood-based panels are closely related to people's daily life as building materials such as home furnishing and decoration, so people have put forward higher requirements for the health and environmental protection functions of wood-based panels. [0003] In CN1974638 literature, a kind of environment-friendly composite floor is disclosed, comprising a wear-resistant layer, a high-...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B27N3/04B27N3/08B27N3/10
Inventor 于文吉余养伦周月任丁华祝荣先
Owner INST OF WOOD INDUDTRY CHINESE ACAD OF FORESTRY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com