Single-component solvent-free damp solidifying polyurethane adhesion agent and method of producing the same
A polyurethane adhesive, moisture-curing technology, used in polyurea/polyurethane adhesives, adhesives, adhesive types, etc., can solve the problems of slow curing speed, low bonding strength, storage stability, etc. The effect of fast speed, high bonding strength and good storage stability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0014] Add 30 parts of polyester polyol (-OH%, hydroxyl value 225) and 30 parts of polyether polyol (model N-210) to the reaction kettle, vacuum dehydrate at 120°C for 2 hours, add 34 parts of TDI (model 80 / 20), Raise the temperature to 85°C-95°C, stir and react for 4 hours, cool down to 50°C, add 0.1 part of catalyst, 0.5 part of silane coupling agent (model KH550), stir for 0.5 hour, and discharge after passing the test.
[0015] The -NCO% of the product is 8-10%. The initial curing speed of the product is 16 hours and the final curing time is 48 hours under the condition of room temperature 20 ℃ and humidity 50%. The bonding strength between aluminum and aluminum is > 25 kg / The storage stability of the product is greater than 12 months.
Embodiment 2
[0017] Add 30 parts of polyester polyol (-OH%, hydroxyl value 225) and 30 parts of polyether polyol (model N-210) to the reaction kettle, vacuum dehydrate at 120°C for 2 hours, add 34 parts of TDI (model 80 / 20), Raise the temperature to 85°C-95°C, stir and react for 4 hours, cool down to 50°C, add 0.5 part of catalyst, 1.0 part of silane coupling agent (model KH550), stir for 0.5 hour, test, and discharge as qualified.
[0018] The -NCO% of the product is 8-10%. The initial curing speed of the product is 3-4 hours under the condition of room temperature 20 ℃ and humidity 50%. The final curing time is 24 hours. The bonding strength between aluminum and aluminum is >25 kg / cm2, the storage stability of the product is greater than 6 months.
Embodiment 3
[0020] Add 40 parts of polyether polyol (model N-330) and 30 parts of polyether polyol (model N-210) to the reaction kettle, vacuum dehydrate at 120°C for 2 hours, add 20 parts of liquefied MDI, TDI (model 80 / 20) 22 part, heated to 85°C-95°C, stirred for 2 hours, added 2 parts of BDO, continued to react for 2 hours, cooled to 50°C, added 0.2 part of catalyst, 0.8 part of silane coupling agent (model KH550), stirred for 0.5 hour, detected , qualified discharge.
[0021] The -NCO% of the product is 9-11%. The initial curing speed of the product is 6 hours and the final curing time is 36 hours under the condition of room temperature 20 ℃ and humidity 50%. The bonding strength between aluminum and aluminum is > 25 kg / square centimeters, the storage stability of the product is greater than 9 months
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com