Abrasion-proof energy-saving polyethylene fishing net

A technology of polyethylene and polyethylene resin, applied in fishing nets, single-component polyolefin artificial filaments, fishing, etc., can solve problems such as poor use and fishing effects, large use limitations, and increased weight of nets, and achieve Enrich the wear-resistant and energy-saving technology and application range of fishing nets, improve the elasticity and fatigue resistance, save plastic materials and energy

Inactive Publication Date: 2009-01-28
EAST CHINA SEA FISHERIES RES INST CHINESE ACAD OF FISHERY SCI
View PDF0 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The defect of high-twist polyethylene fiber fishing net internal twist and external twist is that the breaking strength of the fishing net will be lost by 20% to 30%. And the weight of the fishing net, not only the manufacturing cost is high, but also the weight of the mesh increases by 30%, which greatly increases the cost of using the net, which is equivalent to using 30

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0006] The process flow of the present invention includes mixing masterbatch, batching, melt extrusion, cooling pre-drawing, drawing and setting, winding, thread making, and weaving;

[0007] The masterbatch is prepared according to the following requirements: the content of ultra-high molecular weight silane is 8% to 20%, the content of high molecular weight polyolefin is more than 3% to 5%, the base material of the masterbatch is polyethylene resin, and the appearance of the masterbatch is smooth and uniform in size. The masterbatch is dried for 1 hour at a temperature of 80°C to 90°C;

[0008] The batching is to mix the wear-resistant masterbatch and polyethylene resin according to the weight ratio. The weight of the wear-resistant masterbatch is 2% to 5% of the polyethylene weight. It is selected according to the wear-resistant degree requirements and the content of the wear-resistant masterbatch. Stir the mixture prepared according to the weight ratio evenly in the mixer;...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a polythene fishing net with wear resistance and energy saving and relates to the filed of fishing gear manufacturing. The wear resistance of the fishing net needs to be improved. The invention adopts the preparation technology of the polythene fishing net and is characterized in that ultra-high molecular weight silicane and high molecular weight polyolefin are mixed with master batches of polyvinyl resin in proportion, wear resistant master batches which are blended in proportion and the polyvinyl resin are blended according to weight proportion, the weight of the wear resistant master batches is 2 percent to 5 percent of the weight of the polythene, the mixture is melt-extruded by an extruding machine, the fiber which is melt-extruded is put into a flume to be cooled and pre-drafted, and the cooled monofilament fiber is drafted. The drafting temperature is 90 to 105 DEG C, the drafting multiple is 11 to 13 times, the setting temperature of the drafted monofilament is 90 to 120 DEG C, the set monofilament fiber is coiled by the wrapping tension of 200 plus or minus 30cN and the coiling speed of 120 to 150 meters per min, and the monofilament is made into net wire of the twist number of 36 to 216 twists per meter and is woven into the wear resistant fishing net with the mesh size of 10mm to 1200mm.

Description

Technical field: [0001] The invention belongs to the fishing gear material manufacturing technology. Background technique [0002] Polyethylene (HDPE) fishing nets are damaged due to violent friction with metal and non-metal materials such as stones, cement, steel, and plastics during use. The scrapping and damage of net gear mainly comes from wear and tear, so the service life mainly depends on the wear resistance of its net gear. The existing polyethylene fishing net mainly improves the wear resistance by increasing the twist of the fishing net line when it is twisted. If the wear resistance of the fishing net is increased by about 15% to 20%, it is necessary to increase the twist of the fishing net line by 30%. The defect of high-twist polyethylene fiber fishing net internal twist and external twist is that the breaking strength of the fishing net will be lost by 20% to 30%. And the weight of the fishing net, not only the manufacturing cost is high, but also the weight...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A01K75/00D01D5/08D01F6/04
Inventor 马海有郭亦萍陈雪忠
Owner EAST CHINA SEA FISHERIES RES INST CHINESE ACAD OF FISHERY SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap