Preparation method of bisphenol A polyethenoxy ether toughening agent
A polyoxyethylene ether and toughening agent technology, applied in the field of toughening agents, can solve the problems of low chemical corrosion resistance, low electrical performance, and poor aging resistance, achieve good electrical properties, enhance aging resistance, and improve The effect of flexibility
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0024] Example 1: The preparation method of the bisphenol A polyoxyethylene ether toughening agent of this example is used to prepare the molecular formula: (n=3) product, the reaction equation is:
[0025] The specific steps are:
[0026] a. Prepare 1140 parts by weight of EO monomer in the measuring tank, and put 1100 parts by weight of BPA and 2.5 parts by weight of solid NaCO into the reactor 3 , KOH mixed catalyst, after stirring evenly, close the reactor for many times to exhaust nitrogen;
[0027] b. Begin to add 50 parts by weight of EO dropwise to the solid starter material produced in step a, and perform the first solid-liquid phase reaction. The temperature of the first solid-liquid phase reaction is 20° C., and the reaction time is 30 Min; Then 100 parts by weight of EO was added dropwise to continue the second solid-liquid phase reaction. The temperature of the second solid-liquid phase reaction was 30°C, and the reaction time was 30 Min;
[0028] c. After the seco...
Example Embodiment
[0033] Example 2: The preparation method of the bisphenol A polyoxyethylene ether toughening agent of this example is used to prepare the molecular formula: (n=3) product, the reaction equation is:
[0034] The specific steps are:
[0035] a. Prepare 1145 parts by weight of EO monomer in the measuring tank, and put 1100 parts by weight of BPA and 2.5 parts by weight of solid NaCO into the reactor 3 , KOH mixed catalyst, after stirring evenly, close the reactor for many times to exhaust nitrogen;
[0036] b. Begin to add 50 parts by weight of EO dropwise to the solid starter material produced in step a, and perform the first solid-liquid phase reaction. The temperature of the first solid-liquid phase reaction is 23° C., and the reaction time is 40 Min; Then 100 parts by weight of EO was added dropwise to continue the second solid-liquid phase reaction. The temperature of the second solid-liquid phase reaction was 40°C, and the reaction time was 40 Min;
[0037] c. After the seco...
Example Embodiment
[0041] Example 3: The preparation method of the bisphenol A polyoxyethylene ether toughening agent of this example is used to prepare the molecular formula: (n=3) product, the reaction equation is:
[0042] The specific steps are:
[0043] a. Prepare 1160 parts by weight of EO monomer in the measuring tank, and put 1100 parts by weight of BPA and 2.7 parts by weight of solid NaCO into the reactor 3 , KOH mixed catalyst, after stirring evenly, close the reactor for many times to exhaust nitrogen;
[0044] b. Begin to add 50 parts by weight of EO dropwise to the solid starter material produced in step a to perform the first solid-liquid phase reaction. The temperature of the first solid-liquid phase reaction is 25° C., and the reaction time is 50 Min; Then 100 parts by weight of EO was added dropwise to continue the second solid-liquid phase reaction, the temperature of the second solid-liquid phase reaction was 45°C, and the reaction time was 50 Min;
[0045] c. After the second ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap