Paste composition for printing

A composition and paste technology, which can be used in printing, application, household appliances, etc., and can solve the problems of screen precision reduction, screen short circuit, opening, etc.

A composition and paste technology, which can be used in printing, application, household appliances, etc., and can solve the problems of screen precision reduction, screen short circuit, opening, etc.

CN101432375BInactive Publication Date: 2013-05-08DONGJIN SEMICHEM CO LTD
0 Cites 0 Cited by

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] 15% by weight of methacrylic acid (MA): benzyl acrylate (BA): 2-hydroxyethyl (meth)acrylate (2-HEMA): methyl (meth)acrylate as an acrylate polymer resin (MMA) Polymer resin (weight average molecular weight: 25,000) polymerized in a weight ratio of 30:20:10:40, 10% by weight of M310 (supplied by Miwon Commercial Co., Ltd.) as a cross-linked oligomer: DPHA (supplied by Japan Chemical Co., Ltd.): U-108A (supplied by Shin-Nakamura Chemical Co., Ltd.) cross-linked oligomer mixed in a ratio of 1:2:1, 71% by weight as metal powder Silver and 2% by weight of an amino group-containing organic dispersant as a dispersant were mixed and stirred at room temperature, and finally, a desired paste composition for printing was prepared using a 3-roll mill.

Embodiment 2～3 and comparative example 1～2

[0049] Except that the composition shown in Table 1 below was used in Example 1, the same procedure as in Example 1 was performed to prepare a paste composition for printing.

[0050] The units used in Table 1 are % by weight.

[0051] Table 1

[0052]

[0053] Gravure offset printing was performed using the printing paste compositions prepared in Examples 1 to 3 and Comparative Example 1 or 2 to evaluate printing performance, minimum line width, and pattern directionality, and the results are shown in Table 2 below.

[0054] In the gravure offset printing, each of the paste compositions for printing prepared in Examples 1 to 3 and Comparative Example 1 or 2 was applied to a gravure panel, and the composition was uniformly applied thereon using a doctor blade. , and then transfer the composition on the intaglio panel to the covering (OFF process). Next, the pattern transferred to the cover is cured once using a UV lamp, and the pattern transferred to the cover is t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

This invention provides paste composition for printing, which is particularly characterized by comprising a) 5 to 30 % by weight of an acrylate polymer resin; b) 5 to 30 % by weight of a cross-linking oligomer; c) 0.1 to 5 % by weight of a photopolymerization initiator; and d) 50 to 85 % by weight of a metal powder. The paste composition for printing in accordance with the invention is especially suitable for gravure offset printing capable of directly forming fine pattern, it can fundamentally solve retreatment problems of materials that occur during the manufacturing of electrodes of mesh filters for shielding electromagnetic waves or electrode pattern for plasma display panels using the prior photolithography methods and at the same time, it can satisfy a variety of the properties required as a paste composition each of which is required for printing process so that appropriate offset print performance can be exerted.

Description

technical field [0001] The present invention relates to a paste composition for printing, and more particularly to a paste composition for printing especially suitable for gravure offset printing capable of directly forming fine patterns, which can The problem of material reprocessing that occurs when the electrodes of the mesh filter for shielding electromagnetic waves or the electrode pattern for the plasma display panel is manufactured by engraving, and various properties required for the paste composition can be satisfied at the same time, among which Each is required by the printing process for proper offset performance. Background technique [0002] Recently, with increasing demands for large size, high density, high precision, and high reliability in display devices, various pattern processing technologies are being developed, and research is being conducted on a large number of patterns for forming patterns suitable for the various patterns. The composition of the f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
08 May 2013
Publication
CN101432375B
IPC
C09D11/02; B41M1/10; B41M1/34; C08L33/00; C09D11/033; C09D11/037; C09D11/52; G09F9/00; G09F9/30; H01B1/22; H01B13/00; H05K9/00
CPC
C09D11/03; C09D11/107; C09D11/101; H01J17/49
Inventors
朴赞硕; 金奉玘